The invention discloses a surfacing repair method for F22 material marine BOP shell, which includes: step 1, preheating the repaired parts of BOP shell to be welded, the preheating temperature is 150 50 and step 2, surfacing with ER49 1 as welding material, welding current is 180 200A, welding voltage is 14.5 15V, welding speed is 175 185 mm / min; step 3, tempering after welding. The surfacing treatment method provided by the invention first processes and cleans the worn parts of the BOP shell and preheats the welded repair parts. By controlling the preheating temperature, interlayer temperature, welding current, welding voltage, welding speed and other process parameters as well as the selection of welding materials, the BOP shell can be repaired to the original size, and the welded parts can also reach the BOP shell. Body strength to ensure the safety of wellhead device sealing.
【技术实现步骤摘要】
F22材料海洋防喷器壳体堆焊修复的一种方法
本专利技术涉及F22材料海洋防喷器壳体堆焊修复的一种方法，利用一种堆焊方法来修复海洋石油钻井防喷器本体，恢复防喷器的使用性能，延长防喷器的使用寿命。
技术介绍
防喷器是用于试油、修井、完井等作业过程中关闭井口，防止井喷事故发生，将全封和半封两种功能合为一体，具有结构简单，易操作，耐高压等特点，是油田常用的防止井喷的安全密封井口装置。海洋石油钻井防喷器本体一般用的材料是F22(是美国ASTM材料标准中的一种钢材)，它具备较高的强度和良好的抗海水腐蚀能力，防喷器在使用一段时间后，有些部位会磨损，需要修复，通常用堆焊的方法将磨损处补起来，经过机械加工恢复到原来尺寸精度。
技术实现思路
本专利技术的目的是提供一种防喷器壳体的修复方法，通过堆焊修复，将磨损部位恢复至原来的尺寸精度，以保证安全密封。为达到上述目的，本专利技术提供了一种F22材料海洋防喷器壳体的堆焊修复方法，该方法包含：步骤1，对防喷器壳体的需焊接修复部位进行预热，预热温度150℃±50℃；步骤2，以ER49-1为焊材进行堆焊，焊接电流180-200A，焊接电压14.5-...
【技术保护点】
1.一种F22材料海洋防喷器壳体的堆焊修复方法，其特征在于，该方法包含：步骤1，对防喷器壳体的需焊接修复部位进行预热，预热温度150℃±50℃；步骤2，以ER49‑1为焊材进行堆焊，焊接电流180‑200A，焊接电压14.5‑15V，焊接速度175‑185mm/min；步骤3，焊后回火处理。
【技术特征摘要】
1.一种F22材料海洋防喷器壳体的堆焊修复方法，其特征在于，该方法包含：步骤1，对防喷器壳体的需焊接修复部位进行预热，预热温度150℃±50℃；步骤2，以ER49-1为焊材进行堆焊，焊接电流180-200A，焊接电压14.5-15V，焊接速度175-185mm/min；步骤3，焊后回火处理。2.如权利要求1所述的F22材料海洋防喷器壳体的堆焊修复方法，其特征在于，所述的堆焊包含在防喷器壳体的需焊接修复部位焊接若干层。3.如权利要求2所述的F22材料海洋防喷器壳体的堆焊修复方法，其特征在于，堆焊过程中，层间温度250-300℃。4.如...