The invention discloses a printing conductive silver paste, which comprises the following components: silver powder: 66 70 copies, epoxy resin: 12 15 copies, curing agent: 4 6 copies, accelerator: 0.5 1.2 copies, inactive diluent: 5 6 copies, active diluent: 2 3 copies, adhesion promoter: 1 2 copies, anti-sedimentation agent: 0 1 copies, soluble resin: 1 2 copies. The invention also discloses the preparation method of the printing conductive silver paste. The peeling strength and adhesion of the printing conductive silver paste prepared by the invention are strong, and the preparation of the printing conductive silver paste by the invention has low cost, saves a lot of labor and has high commercial value.
【技术实现步骤摘要】
一种印刷导电银浆及其制备方法
本专利技术涉及导电材料
，尤其涉及一种导电银浆及其制备方法。
技术介绍
印刷导电银浆是专为电阻式和电容式触摸屏回路导线设计的低温烘烤型导电银浆，它是由高性能树脂和导电性极佳的银粉精研制作而成，适合用于ITO膜玻璃上。有着优良的印刷性、导电性、硬度和附着力、抗氧化性能优异等特点。随着电子工业的发展，厚膜导体浆料也随之发生不断更新的发展，作为二十一世纪主要发展方向之一的电子工业，其发展和产品更新速度也将是最快的，新的电子元器件和生产工艺技术将需要新的银粉银浆，因此银粉银浆的品种和数量将不断增加。从技术的角度，为适应电子机器不断轻、小、薄、多功能、低成本，银粉银浆会朝着使用工艺更简化、性能更强、可靠性更高、更低成本化发展，也就是最大程度的发挥银导电性和导热性的优势。电子工业的快速发展，加上国内市场、劳动力等方面的优势，使大陆已成为世界电子元器件的主要制造基地之一，其银粉和银浆的用量也将不断增加。目前银粉、银浆作为一个有发展前景的产业，存在很大的发展空间。关键在于谁能网罗人才、投入更多资金，建立国际一流的生产环境、装备水平。银几乎是为电...
【技术保护点】
1.一种印刷导电银浆，其特征在于，以质量份数计，包含以下组分：银粉：66‑70份；环氧树脂：12‑15份；固化剂：4‑6份；促进剂：0.5‑1.2份；非活性稀释剂：5‑6份；活性稀释剂：2‑3份；附着力促进剂：1‑2份；防沉降剂：0‑1份；溶解树脂：1‑2份。
【技术特征摘要】
1.一种印刷导电银浆，其特征在于，以质量份数计，包含以下组分：银粉：66-70份；环氧树脂：12-15份；固化剂：4-6份；促进剂：0.5-1.2份；非活性稀释剂：5-6份；活性稀释剂：2-3份；附着力促进剂：1-2份；防沉降剂：0-1份；溶解树脂：1-2份。2.根据权利要求所述的一种印刷导电银浆，其特征在于，以质量份数计，包含以下组分：银粉：68份；环氧树脂：13.5份；固化剂：5.55份；促进剂：0.95份；非活性稀释剂：5.6份；活性稀释剂：2.5份；附着力增强剂：1.85份；防沉降剂：0.55份；溶解树脂：1.5份。3.根据权利要求1所述的一种印刷导电银浆，其特征在于，所述的环氧树脂为双酚A型环氧树脂，所述的促进剂为甲基咪唑，所述的固化剂为酸酐类固化剂，所述的非活性吸收剂为乙酸乙酯，所述的防沉降剂为聚酰胺蜡。4.根据权利要求1所述的一种印刷导电银浆，其特征在于，所述的银粉粒径为1～1...
【专利技术属性】
技术研发人员：刘伟，
申请(专利权)人：江西华莲欣科技有限公司，
类型：发明
国别省市：江西,36