本发明专利技术公开了一种防静电薄膜，先对碳纳米管CNTs进行羧基化，然后通过熔融共混法制备PLA/PBAT/CNTs‑COOH复合材料，然后将该复合材料制备成防静电薄膜。本发明专利技术通过纳米材料改性使得本发明专利技术制备包装材料具有良好的抗静电和力学性能，综合性能好，且制备方法简单，具有良好的应用价值，尤其是将CNTs‑COOH引入PLA/PBAT体系中,可在不降低拉伸强度的同时,有效提高冲击强度,降低表面电阻率,可用于静电敏感产品的防静电包装，值得推广。

An Antistatic Film

The invention discloses an anti-static film, which carboxylates carbon nanotubes CNTs, then synthesizes PLA/PBAT/CNTs_COOH composite material by melt blending method, and then synthesizes the composite material into an anti-static film. The packaging material prepared by the invention has good antistatic and mechanical properties, good comprehensive performance, simple preparation method and good application value through modification of nano-materials. Especially, introducing CNTs COOH into PLA/PBAT system can effectively improve impact strength and reduce surface resistivity without reducing tensile strength, and can be used for antistatic of electrostatic sensitive products. Electric packaging is worth popularizing.

【技术实现步骤摘要】
一种防静电薄膜
本专利技术涉及一种防静电薄膜。
技术介绍
电子元件是组成电子产品的基础，特别是针对一些静电敏感的电子元件，气泡袋很容易产生静电，从而导致电子元件的损坏，此外，静电可能导致易燃易爆物品的燃烧、爆炸，危害人民生命财产安全，人们因此需要提出一种更好的方案来解决这个问题。
技术实现思路
本专利技术所要解决的技术问题是提供一种防静电薄膜。本专利技术是通过以下技术方案来实现的：一种防静电薄膜，先对碳纳米管CNTs进行羧基化，然后通过熔融共混法制备PLA/PBAT/CNTs-COOH复合材料，其中，CNTs-COOH的添加量为1.2wt％，然后将该复合材料制备成防静电薄膜。作为优选，具体生产过程是：先对碳纳米管CNTs进行羧基化，然后将PLA和PBAT颗粒放入真空烘箱中，在80℃条件下，干燥4小时，将干燥后的PLA、PBAT和CNTs-COOH加入SU-70M型密炼机中，170℃，50转/分钟，熔融密炼5min得到PLA/PBAT/CNTs-COOH复合材料，其中，PLA和PBAT的比例为7:3，CNTs-COOH在PLA/PBAT/CNTs-COOH复合材料的量为1.0wt％-1.2本文档来自技高网...

【技术保护点】
1.一种防静电薄膜，其特征在于，先对碳纳米管CNTs进行羧基化，然后通过熔融共混法制备PLA/PBAT/CNTs‑COOH复合材料，然后将该复合材料制备成防静电薄膜。

【技术特征摘要】
1.一种防静电薄膜，其特征在于，先对碳纳米管CNTs进行羧基化，然后通过熔融共混法制备PLA/PBAT/CNTs-COOH复合材料，然后将该复合材料制备成防静电薄膜。2.根据权利要求1所述的防静电薄膜，其特征在于，具体生产过程是：先对碳纳米管CNTs进行羧基化，然后将PLA和PBAT颗粒放入真空烘箱中，在80℃条件下，干燥4小时，将干燥后的PLA、PBAT和CNTs-COOH加入SU-70M型密炼机中，170℃，50转/分钟，熔融密炼5min得到PLA/PBAT...