高吸热高亮度瓶级聚酯切片制造技术

本发明专利技术公开了一种高吸热高亮度瓶级聚酯切片，属于聚酯切片技术领域。所述高吸热高亮度瓶级聚酯切片，在聚酯切片中含有氮化钛和硫酸钡，氮化钛在聚酯切片中的重量含量为5～30ppm，硫酸钡在聚酯切片中的重量含量为1～5ppm。本发明专利技术是通过在聚酯切片中加入氮化钛和硫酸钡，从而在提高了瓶级聚酯切片吸收红外加热能量的同时又具有颜色浅，透明度高，乙醛含量低、强度高，抗开裂性好，韧性好，阻隔性好，便于后道加工等特点。

Bottle-grade polyester chips with high heat absorption and brightness

The invention discloses a bottle grade polyester chip with high heat absorption and high brightness, which belongs to the technical field of polyester chip. The bottle grade polyester chip with high heat absorption and high brightness contains titanium nitride and barium sulfate in the polyester chip, the weight content of titanium nitride in the polyester chip is 5-30 ppm, and the weight content of barium sulfate in the polyester chip is 1-5 ppm. By adding titanium nitride and barium sulfate into polyester chips, the bottle-grade polyester chips can absorb infrared heating energy while having the characteristics of light color, high transparency, low acetaldehyde content, high strength, good cracking resistance, good toughness, good barrier and easy processing in the back channel.

【技术实现步骤摘要】
高吸热高亮度瓶级聚酯切片
本专利技术属于聚酯切片
，具体涉及一种高吸热高亮度瓶级聚酯切片。
技术介绍
聚酯是以聚对苯二甲酸乙二醇酯(PET)为代表的热塑性线型饱和聚酯的总称，它的一个重要用途是用于食品包装领域。作为食品包装材料时PET既可制成双向拉伸包装膜，又可制成非晶态瓶坯后再吹塑制得到高强度、高透明的拉伸吹塑瓶，还可以直接挤出成片材后再热成型制得中空容器。PET制品具有透明、耐油、保香、卫生可靠和使用温度范围广等性能，因此在包装领域的用量不断增长。在瓶坯吹制成瓶以前都需要加热到玻璃化温度以上，一般加热使用的是远红外灯加热装置。在切片中加入少量远红外线吸收物质，可以在基本不影响瓶子外观的情况下提高瓶坯远红外吸收能力，从而降低吹瓶的能耗，提高生产效率。我国经济快速增长，各项建设取得巨大成就，但也付出了巨大的资源和环境被破坏的代价，这两者之间的矛盾日趋尖锐，群众对环境污染问题反应强烈。这种状况与经济结构不合理、增长方式粗放直接相关。不加快调整经济结构、转变增长方式，资源支撑不住，环境容纳不下，社会承受不起，经济发展难以为继。因此低能耗的产品是未来的发展方向。目前市场上已经有远红外本文档来自技高网...

【技术保护点】
1.一种高吸热高亮度瓶级聚酯切片，其特征在于，在聚酯切片中含有氮化钛和硫酸钡，氮化钛在聚酯切片中的重量含量为5～30ppm，硫酸钡在聚酯切片中的重量含量为1～5ppm。

【技术特征摘要】
1.一种高吸热高亮度瓶级聚酯切片，其特征在于，在聚酯切片中含有氮化钛和硫酸钡，氮化钛在聚酯切片中的重量含量为5～30ppm，硫酸钡在聚酯切片中的重量含量为1～5ppm。2.根据权利要求1所述的高吸热高亮度瓶级聚酯切片，其特征在于，所述聚酯切片特性粘度为0.8～0...

【专利技术属性】
技术研发人员：陈善冬，
申请(专利权)人：嘉兴市天悦包装有限公司，
类型：发明
国别省市：浙江,33