本发明专利技术提供显影辊及其制造方法，该显影辊具备包含内层和外层的辊主体，比现状进一步改善了各种特性，该内层具有多孔质结构，该外层由非多孔质且无缝的管构成。显影辊(1)具备包含多孔质结构的内层(2)和外层(4)的辊主体(5)，该多孔质结构的内层(2)由包含乙丙系橡胶、石蜡系油和DBP吸油量为400cm

Development Roller and Its Manufacturing Method

The invention provides a developing roll and a manufacturing method thereof. The developing roll has a roller body comprising an inner layer and an outer layer, which further improves various characteristics compared with the present situation. The inner layer has a porous structure and the outer layer is composed of a non-porous and seamless tube. The development roll (1) has an inner layer (2) containing a porous structure and a roller body (5) containing an outer layer (4). The inner layer (2) of the porous structure absorbs 400 cm oil by containing ethylene propylene rubber, paraffin oil and DBP.

【技术实现步骤摘要】
显影辊及其制造方法
本专利技术涉及组装至利用电子照相法的成像装置中进行使用的显影辊及其制造方法。
技术介绍
在激光打印机、静电式复印机、普通纸传真机装置或它们的复合设备等利用电子照相法的成像装置中，作为显影方式，非磁性单成分显影方式正成为主流。在非磁性单成分显影方式中，使调色剂从显影辊与调色剂量控制刮刀之间通过，一边使其摩擦带电，一边使其负载于显影辊的外周面，由此在该表面形成调色剂层。接着，使形成的调色剂层直接接触形成有静电潜像的感光体的表面，由此使调色剂选择性地从调色剂层移动到静电潜像，显影为调色剂像。或者，有时也使调色剂层与感光体的表面在维持非接触的状态下接近，由此使调色剂选择性地从调色剂层移动(飞行)到静电潜像，显影为调色剂像。作为显影辊，例如通常使用具备非多孔质且单层的辊主体的显影辊，其中，在橡胶中与用于使该橡胶交联的交联成分一起混配电子导电性导电剂和/或离子导电性导电剂而赋予其半导电性，将所得到的橡胶组合物成型为筒状，并且使橡胶交联，从而形成该辊主体。但是，上述现有的显影辊的辊主体的硬度比较高，因此调色剂有可能因摩擦而发生粉碎等劣化，形成的图像有可能粗糙。另外，有时外添剂的本文档来自技高网...

【技术保护点】
1.一种显影辊，其具备辊主体，该辊主体包含筒状的内层和设置于所述内层外周的外层，所述内层由包含乙丙系橡胶、石蜡系油和DBP吸油量为400cm3/100g以上的炭黑的半导电性橡胶组合物构成，具有多孔质结构；所述外层由半导电性的无缝管构成，为非多孔质，包含聚氨酯系热塑性弹性体、炭黑和中心粒径为5μm以上20μm以下的交联聚甲基丙烯酸甲酯颗粒，在测定温度23℃，所述聚氨酯系热塑性弹性体的日本工业标准JIS K7311‑1995中规定的A型硬度计硬度为93以下。

【技术特征摘要】
2017.06.30 JP 2017-1289671.一种显影辊，其具备辊主体，该辊主体包含筒状的内层和设置于所述内层外周的外层，所述内层由包含乙丙系橡胶、石蜡系油和DBP吸油量为400cm3/100g以上的炭黑的半导电性橡胶组合物构成，具有多孔质结构；所述外层由半导电性的无缝管构成，为非多孔质，包含聚氨酯系热塑性弹性体、炭黑和中心粒径为5μm以上20μm以下的交联聚甲基丙烯酸甲酯颗粒，在测定温度23℃，所述聚氨酯系热塑性弹性体的日本工业标准JISK7311-1995中规定的A型硬度计硬度为93以下。2.如权利要求1所述的显影辊，其中，所述乙丙系橡胶为三元乙丙橡胶。3.如权利要求1或2所...

【专利技术属性】
技术研发人员：野尻和纪，
申请(专利权)人：住友橡胶工业株式会社，
类型：发明
国别省市：日本,JP