A method for making rock samples containing natural three-dimensional cracks is presented. First, the natural three-dimensional crack template is made, then the natural three-dimensional crack template is scanned by morphology, and finally, the model specimen containing cracks is poured. The invention provides a method for making a natural three-dimensional crack template, and the size of the model sample can vary from centimeter level to meter level. The idea is simple, the logic is clear, the steps are clear and the operation is simple. It provides a new idea for the replication of natural cracks and the manufacture of rock samples containing natural three-dimensional cracks.
【技术实现步骤摘要】
一种含天然三维裂隙类岩石试样的制作方法
本专利技术涉及一种岩石试样制作方法,尤其是一种含天然三维裂隙类岩石试样的制作方法,适用于岩石力学与工程
技术介绍
裂隙岩体是水利、采矿、交通、能源、国防等行业中最常见、最重要的介质之一。由于成岩作用及地质构造运动,工程实际中面对的岩体中都存在各种形式的裂隙。为了对天然三维裂隙的力学和水理性质进行研究,制作含有天然三维裂隙的类岩石模型试样成为了重要环节。目前,公知的对于含三维裂隙岩体模型的制作方法主要有两大类。第一大类是通过在浇注模型的模具中设置各种形式的插片,但这类方法获得的裂隙一般为平面,与天然岩体所表现出的具有不同粗糙程度的特征具有巨大的差异。第二大类是利用CT扫描和3D打印技术,通过这一类方法可以得到含单一粗糙面的裂隙岩体,但是天然岩体中的裂隙是由多个不同特征的粗糙裂隙面构成的三维裂隙面网络,同时需要利用CT扫描和3D打印的设备,成本过于昂贵,而且利用该类方法得到的试样尺寸一般较小。
技术实现思路
为了克服现有技术的上述不足,本专利技术提供一种含天然三维裂隙类岩石试样的制作方法,通过该方法能够获得含天然、三维裂隙的类岩石试样,步骤简单,成本低。本专利技术解决其技术问题采用的技术方案是:首先制作天然三维裂隙模板,之后对天然三维裂隙模板进行形态扫描,最后浇筑含裂隙模型试样。相比现有技术,本专利技术的一种含天然三维裂隙类岩石试样的制作方法,率先提出了一种能够以较简单的方法制作含天然三维裂隙的类岩石模型试样,步骤简单,成本低,试验模拟效果好,模型试样的尺寸可以在厘米级到米级范围内变化,为裂隙岩体模型制作提供了一个 ...
【技术保护点】
1.一种含天然三维裂隙类岩石试样的制作方法,其特征是:首先制作天然三维裂隙模板(5),之后对天然三维裂隙模板(5)进行形态扫描,最后浇筑含裂隙模型试样。
【技术特征摘要】
1.一种含天然三维裂隙类岩石试样的制作方法,其特征是:首先制作天然三维裂隙模板(5),之后对天然三维裂隙模板(5)进行形态扫描,最后浇筑含裂隙模型试样。2.根据权利要求1所述的一种含天然三维裂隙类岩石试样的制作方法,其特征是,所述制作天然三维裂隙模板(5)的步骤如下:首先,从工程现场收集含裂隙岩石块体并打磨成立方体试块(1);利用五块与立方体试块(1)表面相同大小的金属板(4)封堵立方体试块(1)的四个侧面和下底面;然后,将聚乙烯塑料加热至熔融状态成为聚乙烯材料(3),并从没有金属板(4)封堵的顶面向立方体试块(1)中的天然裂隙(2)内快速注入聚乙烯材料(3);随着温度的降低,聚乙烯材料(3)逐渐凝固;当聚乙烯材料(3)完全凝固后,撤除立方体试块(1)上的金属板(4);最后,对充聚乙烯材料(3)后的立方体试块(1)进行破碎,...
【专利技术属性】
技术研发人员:刘日成,靖洪文,蔚立元,何明,
申请(专利权)人:中国矿业大学,
类型:发明
国别省市:江苏,32