The invention relates to the field of brazing technology, in particular to the brazing process of an electrothermal substrate. The steps of the brazing process are as follows: a) at room temperature, micron pure nickel powder and terpineol solvent are put into the mixer and stirred into liquid nickel powder, the ratio of micron pure nickel powder to terpineol solvent is 1:2; b) the liquid nickel powder is directly pointed at the welding point of the electrothermal substrate and dried; c) the dried electrothermal substrate is joined with solder and nickel wire into the electric furnace to complete the welding. The invention directly uses nickel powder to coat on the surface and metallizes the nickel powder through temperature, thus achieving the purpose of brazing. Avoid the use of chemical solvents and the treatment of solvent wastewater, which is conducive to the protection of the environment.
【技术实现步骤摘要】
电热基板的钎焊工艺
本专利技术涉及钎焊
，尤其是电热基板的钎焊工艺。
技术介绍
现有技术中，在电热基板上钎焊镍丝时需要在电热基板的焊接点上镀上一层金属层(其中金属为钨)，之后才能将焊料和镍丝放置在该金属层上，推入温度为800度的电炉里进行焊接。如果不在焊接点上镀上一层金属层，则无法使焊料和镍丝牢固的粘在焊接点上。现有的处理工艺是用几种金属溶剂配比成活化液和镀液分三步(活化，镀层，清洗)完成的，而且生产过程中产生的废液处理需要繁琐的环保处理方式。耗时耗力，成本很高，不利于企业竞争。
技术实现思路
本专利技术要解决的技术问题是：为了解决现有的
技术介绍
中描述的技术问题，本专利技术提供了一种电热基板的钎焊工艺，通过直接采用镍粉涂在上面，通过温度使镍粉金属化，从而达到钎焊的目的。避免使用化学溶剂及处理溶剂的废水，有利于保护环境。本专利技术解决其技术问题所采用的技术方案是：一种电热基板的钎焊工艺，该钎焊的步骤为：a)常温下将微米级纯镍粉和松油醇溶剂放入搅拌机内搅拌成液态状镍粉，微米级纯镍粉与松油醇溶剂的比例为1:2；b)将液态状镍粉直接点在电热基板的焊接点上并烘干；c)将烘...
【技术保护点】
1.一种电热基板的钎焊工艺，其特征在于，该钎焊的步骤为：a)常温下将微米级纯镍粉和松油醇溶剂放入搅拌机内搅拌成液态状镍粉，微米级纯镍粉与松油醇溶剂的比例为1:2；b)将液态状镍粉直接点在电热基板的焊接点上并烘干；c)将烘干后的电热基板加上焊料与镍丝进入电炉完成焊接。
【技术特征摘要】
1.一种电热基板的钎焊工艺，其特征在于，该钎焊的步骤为：a)常温下将微米级纯镍粉和松油醇溶剂放入搅拌机内搅拌成液态状镍粉，微米级纯镍粉与松油醇溶剂的比例为1:2；b)将液态状镍粉直接点在电热基板的焊接点上并烘干；c)将烘干后的电热基板加上焊料与镍丝进入电炉完成焊接。2.根据权利要求1所述的电热基板的钎焊工艺，其特征在于：在步骤a)中，所述搅拌时间为20分钟。3.根据权利要求1所述的电热基板的钎焊工艺，...
【专利技术属性】
技术研发人员：赵基农，
申请(专利权)人：宜兴市美盛电器有限公司，
类型：发明
国别省市：江苏,32