The invention discloses an additive for negative lead paste of lead-acid battery, which is composed of the following components measured by mass percentage: barium sulfate 37-65%, sodium lignosulfonate 15-30%, polyester staple fiber 2.6-8% and mixed carbon material 17-35%. The mixed carbon material contains 55% acetylene black, 35% plant high temperature carbide and 10% expanded graphite. The method adds an appropriate amount of additives to the conventional negative lead paste, which significantly increases the content of sodium lignosulfonate, mixed carbon material and barium sulfate. Especially, as recrystallized nucleus, barium sulfate exists in components, which is isomorphic with lead sulfate at discharge. Because barium sulfate is highly dispersed in negative lead paste, it provides a large number of nuclei for lead sulfate during discharge, thus inhibiting the formation of lead sulfate on the surface of lead crystal, which improves the discharge performance at low temperature.
【技术实现步骤摘要】
用于铅酸蓄电池负极铅膏的添加剂
本专利技术属于电化学电源
的一项技术方案，具体地讲，本专利技术涉及一种铅酸蓄电池负极铅膏，特别是用于铅酸蓄电池负极铅膏的添加剂。
技术介绍
随着制造业的技术进步和市场需求的增加，配套铅酸蓄电池的设备或装置越来越多，当然使用环境也越来越复杂，故对配套的铅酸蓄电池性能也有了更高的要求，特别是低温性能已上升为必检项目。业内专业技术人员悉知，铅酸蓄电池低温性能主要取决于负极铅膏的配置，现有技术配置的铅膏仅注重25℃10小时率容量值符合行业相关标准要求，而不考虑是否满足0℃10小时容量要求。因此，现有技术产品作为商品交付给用户时，难以通过低温性能验收关，易引发供需双方的纠纷。
技术实现思路
本专利技术主要针对现有技术的不足，重点达到铅酸蓄电池0℃10小时率容量与25℃10小时率容量比≥0.80的目标。提出一种用于铅酸蓄电池负极铅膏的添加剂，该添加剂组分简单、原料易得、成本低廉、混合容易，使用该添加剂能够明显改善电池的低温性能。本专利技术通过下述技术方案实现技术目标。用于铅酸蓄电池负极铅膏的添加剂，其改进之处在于它由下列按质量百分比计量的组分...
【技术保护点】
1.一种用于铅酸蓄电池负极铅膏的添加剂，其特征在于它由下列按质量百分比计量的组分组成：硫酸钡37～65%、木素磺酸钠15～30%、涤纶短纤维2.6～8%和混合碳材料17～35%。
【技术特征摘要】
1.一种用于铅酸蓄电池负极铅膏的添加剂，其特征在于它由下列按质量百分比计量的组分组成：硫酸钡37～65%、木素磺酸钠15～30%、涤纶短纤维2.6～8%和混合碳材料17～35%。2.根据权利要求1所述的用于铅酸蓄电池负极铅膏的添加剂，其特征在于：所述混合碳材料由下列按质量百分比计量的乙炔黑55%、植物高温碳化物35%和膨胀石墨10%组分组成。3.根据权利要求1所述的用于铅酸蓄电池负极铅膏的添...