The invention discloses a preparation method of binder, which first stirs polyacrylic acid into deionized water until it dissolves completely, and then adds pyrene substitutes to polyacrylic acid aqueous solution, keeps the system in inert atmosphere, stirs and slowly warms up to 120-180 degrees C, and continues to react for 6-10 hours to prepare the product; finally, after centrifugal water washing, the product is baked. Dry, make the binder. By introducing pyrene functional group into PAA, the bonding force between PAA and active substance was increased, and the interaction force between active substance and conductive carbon was also increased, so the cycle performance of lithium ion battery was improved.
【技术实现步骤摘要】
粘结剂及其制备方法、锂离子电池负极片
本专利技术涉及锂离子电池生产领域，具体涉及一种粘结剂及其制备方法，还涉及一种锂离子电池负极片。
技术介绍
随着便携电子设备和电动汽车的发展，人们对锂离子电池的能量密度的要求也在日益提高。目前商业化应用最广的石墨类负极材料的理论比容量只有372mAh/g，已不能满足高能量密度锂离子电池的发展需求，此外它的嵌锂电位非常接近锂的沉积电势，给电池带来了巨大的安全隐患。近几年大量的工作集中在硅基负极材料上，原因是硅超高的理论容量(4200mAh/g)，但是纳米硅作为负极材料的缺陷是电池在充放电过程中伴随很大的体积效应导致硅颗粒的粉化，从而与导电剂之间失去了电接触，破坏了整个电极结构，造成了电池容量的衰减和极差的循环性能。为了提高硅负极的性能及它的循环寿命，选择一款合适的高性能粘结剂是一种非常重要的方法，目前常见的粘结剂有PAA(聚丙烯酸)、CMC(羧甲基纤维素)/SBR(丁苯橡胶)、海藻酸钠、壳聚糖、PI(聚酰亚胺)、PAI等，其中PAA、PVA和海藻酸钠型的粘结剂分子链上含有大量的羧基，与活性物质和集流体之间的可以形成很强的相互作用，...
【技术保护点】
1.一种粘结剂的制备方法，其特征在于：包括以下步骤：a、将聚丙烯酸加入去离子水中搅拌至溶解完全，制得聚丙烯酸水溶液；b、向聚丙烯酸水溶液中加入芘基取代物，将体系保持在惰性气氛中，搅拌并缓慢升温至120~180℃，继续反应6~10h，制得产物；c、将产物离心水洗后，烘干，制得粘结剂。
【技术特征摘要】
1.一种粘结剂的制备方法，其特征在于：包括以下步骤：a、将聚丙烯酸加入去离子水中搅拌至溶解完全，制得聚丙烯酸水溶液；b、向聚丙烯酸水溶液中加入芘基取代物，将体系保持在惰性气氛中，搅拌并缓慢升温至120~180℃，继续反应6~10h，制得产物；c、将产物离心水洗后，烘干，制得粘结剂。2.如权利要求1所述的制备方法，其特征在于：所述聚丙烯酸的分子量为5000~100000，所述聚丙烯酸与所述芘基取代物的重量比为3:1~5:1。3.如权利要求1所述的制备方法，其特征在于：所述聚丙烯酸水溶液的质量分数为5~20%。4.如权利要求1所述的制备方法，其特征在于：所述芘基取代物为芘基取代的烷基醇、芘基取代的含有氨基的脂肪烃或芘基取代的含有环氧基团的脂肪烃。5.如权利要求4所述的制备方法，其特征在于：所述芘基取代的烷基醇中碳原子数4≤n≤10...