The invention discloses a method for preparing foamed nickel electrode coated with cobalt hydroxide surface. The method comprises: putting nickel hydroxide in 0.1~0.5 mol/L cobalt chloride solution, slowly dropping 0.5~1 mol/L potassium hydroxide solution under stirring at 30~40 (?) C, transferring the filtered solid to 5~7 mol/L potassium hydroxide solution after precipitation, adding sodium hypochlorite at constant temperature of 60~80 (?) After chemical treatment, the product was washed to neutral, dried, grinded and sifted to obtain foamed nickel electrode coated with cobalt hydroxide. The invention also discloses a foamed nickel electrode coated on the surface of cobalt hydroxide prepared by the above method. The foamed nickel electrode coated on the surface of cobalt hydroxide prepared by chemical oxidation method has high stability and capacity retention.
【技术实现步骤摘要】
一种羟基氧化钴表面包覆的发泡镍电极及其制备方法
本专利技术属于镍氢电池
,具体涉及一种羟基氧化钴表面包覆的发泡镍电极及其制备方法。
技术介绍
镍氢电池由于其较高的能量密度和功率密度、较长的循环稳定性和低廉的价格,在便携式用电器和电动车中广泛应用。镍氢电池使用发泡镍电极,发泡镍电极的导电网络由发泡镍基体和羟基氧化钴构成。目前,发泡镍电极中的羟基氧化钴主要由混合到镍电极中的氧化钴转化而来,碱性介质中,氧化钴经过溶解、沉积包覆在氢氧化镍表面,在首次充电时转化为具有良好导电性能的羟基氧化钴(即电化学氧化)。然而,如果发泡镍电极的放电电位低于其正常工作电位较多,羟基氧化钴会被还原并转化为难溶并且活性低的钴化合物,导致发泡镍电极导电网络被破坏,造成充放电容量不可逆损失。因此,需要制备稳定性较高的羟基氧化钴表面包覆的发泡镍电极。
技术实现思路
专利技术目的:本专利技术的目的是提供一种制备羟基氧化钴表面包覆的发泡镍电极的方法,制备出稳定性较高的羟基氧化钴表面包覆的发泡镍电极。技术方案:本专利技术提供一种制备羟基氧化钴表面包覆的发泡镍电极的方法,该方法包括:将氢氧化镍置于0.1~0.5mol/L的氯化钴溶液中,30~40℃搅拌下缓慢滴加0.5~1mol/L的氢氧化钾溶液,沉淀完全后过滤得到的固体转移到5~7mol/L的氢氧化钾溶液中,60~80℃恒温下加入次氯酸钠充分氧化后,将得到的产物洗涤至中性,干燥,研磨,过筛,即得羟基氧化钴表面包覆的发泡镍电极。优选地,加入的次氯酸钠的物质的量为氯化钴的2~3倍。本专利技术另一方面提供一种羟基氧化钴表面包覆的发泡镍电极,该羟基氧化钴 ...
【技术保护点】
1.一种化学氧化法制备羟基氧化钴表面包覆的发泡镍电极的方法,其特征在于,该方法包括:将氢氧化镍置于0.1~0.5mol/L的氯化钴溶液中,30~40℃搅拌下缓慢滴加0.5~1mol/L的氢氧化钾溶液,沉淀完全后过滤得到的固体转移到5~7mol/L的氢氧化钾溶液中,60~80℃恒温下加入次氯酸钠充分氧化后,将得到的产物洗涤至中性,干燥,研磨,过筛,即得羟基氧化钴表面包覆的发泡镍电极。
【技术特征摘要】
1.一种化学氧化法制备羟基氧化钴表面包覆的发泡镍电极的方法,其特征在于,该方法包括:将氢氧化镍置于0.1~0.5mol/L的氯化钴溶液中,30~40℃搅拌下缓慢滴加0.5~1mol/L的氢氧化钾溶液,沉淀完全后过滤得到的固体转移到5~7mol/L的氢氧化钾溶液中,60~80℃恒温下加入次氯酸钠充分氧化后,将得到的产...