The invention discloses a wear-resistant and flame-retardant polyurethane coating, which comprises water-borne polyurethane resin, hydroxymethyl phenylphosphamide carboborane, modified red mud powder, charring agent, dispersant, adhesion promoter, ultraviolet absorbent, thickener, wetting agent and leveling agent. The modified red mud powder was prepared by following processes: adding red mud to acidic aqueous solution, drying to produce red mud powder with neutral PH value; adding red mud powder to ball mill to produce red mud powder; adding red mud powder to modifier, heating to prepare modified red mud powder. The polyurethane coating of the invention has high oxygen index, good flame retardancy and wear resistance.
【技术实现步骤摘要】
一种耐磨阻燃聚氨酯涂料
本专利技术涉及阻燃
,尤其涉及一种耐磨阻燃聚氨酯涂料。
技术介绍
聚氨脂涂料是由脂肪酸聚氨酯树脂、颜料、助剂、溶剂组成的漆料为羟基组份及由异氰酸酯为另一组份的双组份自干涂料,其特点在于漆膜装饰性能优异、干燥快、耐化学品性能好、附着力强。聚氨酯树脂的氧指数低,为易燃燃材料,燃烧时低烟,并伴有熔融落滴,随着应用范围和阻燃要求的不断提高,需要对其进行阻燃改性处理。如何制备一种性能优异的阻燃聚氨酯涂料是目前急需解决的技术问题。
技术实现思路
基于
技术介绍
存在的技术问题,本专利技术提出了一种耐磨阻燃聚氨酯涂料,氧指数高,耐磨和阻燃性能好。本专利技术提出一种耐磨阻燃聚氨酯涂料,其原料按重量份包括:水性聚氨酯树脂80-120份,羟甲基苯基次磷酰胺碳硼烷10-20份,改性赤泥微粉5-10份,成炭剂2-5份,分散剂1-2份,附着力促进剂1-2份,紫外线吸收剂1-2份,增稠剂1-3份,润湿剂1-3份,流平剂0.5-1.5份。优选地,改性赤泥粉采用如下工艺制备:将赤泥加入酸性水溶液中酸化处理后,干燥制得PH值为中性的赤泥粉;将赤泥粉加入球磨机球磨制得赤泥微粉;将赤泥微粉加入改性剂,升温改性制得改性赤泥微粉。优选地,酸化处理温度为90-100℃,时间为2-4h。优选地,赤泥微粉的粒径为0.1-1μm。优选地,赤泥微粉和改性剂的重量比为100:2-6。优选地,改性剂原料按重量份包括:硬脂酸20-30份,钛酸酯30-40份,乙烯基硅烷30-40份。优选地,升温改性的温度为120-140℃,时间为0.5-1h。优选地,羟甲基苯基次磷酰胺碳硼烷、纳米赤泥微粉、成 ...
【技术保护点】
1.一种耐磨阻燃聚氨酯涂料,其特征在于,其原料按重量份包括:水性聚氨酯树脂80‑120份,羟甲基苯基次磷酰胺碳硼烷10‑20份,改性赤泥微粉5‑10份,成炭剂2‑5份,分散剂1‑2份,附着力促进剂1‑2份,紫外线吸收剂1‑2份,增稠剂1‑3份,润湿剂1‑3份,流平剂0.5‑1.5份。
【技术特征摘要】
1.一种耐磨阻燃聚氨酯涂料,其特征在于,其原料按重量份包括:水性聚氨酯树脂80-120份,羟甲基苯基次磷酰胺碳硼烷10-20份,改性赤泥微粉5-10份,成炭剂2-5份,分散剂1-2份,附着力促进剂1-2份,紫外线吸收剂1-2份,增稠剂1-3份,润湿剂1-3份,流平剂0.5-1.5份。2.根据权利要求1所述耐磨阻燃聚氨酯涂料,其特征在于,改性赤泥粉采用如下工艺制备:将赤泥加入酸性水溶液中酸化处理后,干燥制得PH值为中性的赤泥粉;将赤泥粉加入球磨机球磨制得赤泥微粉;将赤泥微粉加入改性剂,升温改性制得改性赤泥微粉。3.根据权利要求2所述耐磨阻燃聚氨酯涂料,其特征在于,酸化处理温度为90-100℃,时间为2-4h。4.根据权利要求...