The present invention provides a modified graphene oxide/water-borne epoxy resin composite coating and its preparation method, which consists of 10 20 parts of water-borne epoxy resin, 20 40 parts of curing agent, 30 40 parts of deionized water, 0.6 1 part of additives, and 0.01 0.03 parts of silicon dioxide/graphene oxide. By modifying graphene oxide with potassium sodium silicate, the surface of graphene oxide is loaded with silicon dioxide, which further improves its dispersion in water. Then it is added into the waterborne epoxy resin coating system, effectively remedying the defects of epoxy resin itself, and a coating with excellent performance has been invented.
【技术实现步骤摘要】
一种改性氧化石墨烯/水性环氧树脂复合涂料及其制备方法
本专利技术涉及氧化石墨烯的改性，及其在水中的分散和在涂料中的应用领域，特别涉及一种改性氧化石墨烯/水性环氧树脂复合涂料及其制备方法。
技术介绍
环氧树脂涂料自身拥有诸多突出的性能，包括良好的附着力，优异的耐化学性能等，这使得其在底漆、地坪漆、防腐漆等领域有着广阔市场。但环氧树脂也存在一定缺陷，例如较差的耐候性，较低的硬度，尤其对于水性环氧树脂来讲，成膜过程中，随着溶剂水的挥发，极易形成针孔，这在某种程度上也限制了其应用。氧化石墨烯作为石墨烯的衍生物，在保留石墨烯二维结构的基础上，又接枝上部分含氧官能团，包括羟基、羧基、环氧基等，这使得氧化石墨烯具有比石墨烯更大的活性和更好的相容性。因此，将氧化石墨烯作为填料加到涂料中改善漆膜性能也成为研究的热点。不过由于氧化石墨烯片层结构的特点，较大的层间范德华力和碳原子间离域π键的作用，再结合涂料的实际情况，通常在调配好后数天甚至数月才施工，当前氧化石墨烯的相容性还不足以满足需求，所以很多人将氧化石墨烯进行改性，发现改性后的氧化石墨烯拥有更出色的分散效果。现阶段所用的改性试剂...
【技术保护点】
1.一种改性氧化石墨烯/水性环氧树脂复合涂料，其特征在于，由如下重量份的原料组成:
【技术特征摘要】
1.一种改性氧化石墨烯/水性环氧树脂复合涂料，其特征在于，由如下重量份的原料组成:其中，二氧化硅/氧化石墨烯的制备工艺如下:将氧化石墨烯，钾水玻璃，无水乙醇，去离子水混合、超声处理一段时间，再在室温下机械混合一段时间，离心、洗涤，干燥，即得二氧化硅/氧化石墨烯。2.如权利要求1所述的涂料，其特征在于，所述氧化石墨烯，钾水玻璃，无水乙醇，去离子水的质量比为0.02-0.03:0.4-0.6:40-42:48-50。3.如权利要求1所述的涂料，其特征在于，所述超声处理条件为:300-350W下超声20-30min。4.如权利要求1所述的涂料，其特征在于，所述钾水玻璃的模数为3.3，波美度为40。5.如权利要求1所述的涂料，其特征在于，所述固化剂为水性环氧树脂固化剂。6.如权利要求1所述的涂料，其特征在于，所述助剂...
【专利技术属性】
技术研发人员：石元昌，宋伯钧，刘庆东，姚慧玲，
申请(专利权)人：山东大学，
类型：发明
国别省市：山东,37