The invention provides a ceramic glaze sensitizing paint, which is made of the following components: epoxy resin solution: 25-26 copies; linoleic acid: 25.5-26 copies; zirconium ceramic powder: 0.8-1.0 copies; lead-free pearlescent slurry: 0.6-0.8 copies; maleic anhydride: 3.5 copies; defoamer: 0.3-0.4 copies; butanol: 7.3 copies; ethyl ester: 37-37.2 copies. The ceramic glaze sensitizing paint in the invention has high brightness, smooth and photolysis paint film, water washing resistance, dry cleaning and ironing film layer does not wrinkle. The experimental results show that the color fastness of the ceramic glaze sensitive paint in the present invention to water washing and dry cleaning is above 4 levels. The invention also provides a preparation method of ceramic glaze-sensitive buttons.
【技术实现步骤摘要】
一种陶瓷釉感漆及陶瓷釉感钮扣的制备方法
本专利技术属于服装用品生产
，尤其涉及一种陶瓷釉感漆及陶瓷釉感钮扣的制备方法。
技术介绍
钮扣作为一种服装的附属品，除了对其功能的要求之外，钮扣在服装造型的艺术上，被称为“服装的眼睛”，因此，钮扣的使用足以成为服饰的“点睛”之笔。从材质上看，钮扣可分为塑料钮扣、金属钮扣、真贝钮扣、陶瓷钮扣等，其中，陶瓷钮扣是由瓷质材料经烧结、上釉、表面饰花再与金属底托组合而成，陶瓷钮扣经过上釉处理之后，钮扣表面饰有花纹，色彩鲜艳，亮度高，装饰效果十分明显，而且陶瓷材料有很高的表面硬度，耐磨性优越。但是由于受到生产方式及工艺水平的限制，生产批量不大，成本偏高，而且在服装洗涤过程中易碎裂，实用性较差。因此，对一些材质更为耐用的钮扣表面进行表面处理，使其呈现陶瓷釉感，得到的钮扣同时具备耐用性和美观性，是装饰性钮扣的发展趋势。目前已批量应用生产的产品表面效果主要是采用镀膜方式仿制而成。方法是：先将各类材质的半成品钮扣产品进行常规抛光处理，后超声波清洗，脱水烘干后，再进行UV油漆喷涂处理，待钮扣表面漆膜成膜后，再采用光学镀膜工艺处理形成钮扣表面...
【技术保护点】
1.一种陶瓷釉感漆，由以下重量份数的组分制成：环氧树脂液：25～26份；亚麻仁油酸：25.5～26份；锆瓷粉：0.8～1.0份；无铅珠光浆：0.6～0.8份；顺丁烯二酸酐：3.5份；消泡剂：0.3～0.4份；丁醇：7.3份；乙酯：37～37.2份。
【技术特征摘要】
1.一种陶瓷釉感漆，由以下重量份数的组分制成：环氧树脂液：25～26份；亚麻仁油酸：25.5～26份；锆瓷粉：0.8～1.0份；无铅珠光浆：0.6～0.8份；顺丁烯二酸酐：3.5份；消泡剂：0.3～0.4份；丁醇：7.3份；乙酯：37～37.2份。2.根据权利要求1所述的陶瓷釉感漆，其特征在于，所述锆瓷粉的粒径为2000～4000目。3.根据权利要求1所述的陶瓷釉感漆，其特征在于，所述环氧树脂液的质量浓度为30～45％。4.根据权利要求1所述的陶瓷釉感漆，其特征在于，所述消泡剂为聚氧乙烯聚氧丙醇胺醚。5.一种陶瓷釉感钮扣的制备方法，包括以下步骤：将半成品钮扣喷涂陶瓷釉感漆，烘干后...
【专利技术属性】
技术研发人员：林强，朱陈彪，李宗慧，
申请(专利权)人：浙江伟星实业发展股份有限公司，
类型：发明
国别省市：浙江,33