A formula for the preparation of insulating skin for cables is provided with the following raw materials: 60-65 phr of styrene-butadiene rubber, 9-10 phr of zinc oxide, 2-4 phr of antioxidant, 8-15 phr of plasticizer, 8 phr of anti-aging agent and 115-1135 phr of filler. The antioxidant is pentaerythritol ester with tetramethyl-beta (3,5-di-tert-butyl-4-hydroxyphenyl) propionate; the plasticizer is 52 degree chlorinated paraffin and phthalic acid. A mixture of dioctyl ester, N isopropyl -p-phenylenediamine as anti-aging agent, talc powder and calcium carbonate as filler, and an insulating skin for cables of the present invention have good anti-aging properties.
【技术实现步骤摘要】
一种用于电缆的绝缘皮制备配方
本专利技术涉及一种用于一种用于电缆的绝缘皮制备配方。
技术介绍
橡套电缆由于其独特的机械性能与物理性能被很多领域的产品所采用,因而其分类众多,比如:通用型、电焊机、电力、船用、矿用、风能,核能等等。但是电缆在应用的过程中由于外界因素的影响和内部电流的影响,绝缘皮老化在所难免。
技术实现思路
本专利技术的目的是为了解决以上现有技术的不足,提供一种用于电缆的绝缘皮制备配方,该绝缘皮具有抗老化性能强的特点。本专利技术为一种用于电缆的绝缘皮制备配方,其特征在于,按重量份,其原料组成如下:抗氧剂为为四[甲基-β-(3,5-二叔丁基-4-羟基苯基)丙酸酯]季戊四醇酯;增塑剂为52度氯化石蜡和邻苯二甲酸二辛脂的混合物;防老化剂为N-异丙基-基对苯二胺;填充剂为滑石粉和碳酸钙的混合物。优选的,按重量份,其原料组成如下:丁苯橡胶64份、氧化锌10份、抗氧剂2份、增塑剂13份、防老化剂8份、充剂135份。优选的,按重量份,其原料组成如下:丁苯橡胶63份、氧化锌9份、抗氧剂2份、增塑剂12份、防老化剂8份、充剂125份。有益效果:使用这种绝缘皮,能有有效提高电缆强度,延长电缆的使用寿命,改善橡胶材料的硫化特性,力学性能,耐热氧老化性,显著提高了材料的抗老化性。具体实施方式为了加深对本专利技术的理解,下面将结合实施例对本专利技术作进一步详述,该实施例仅用于解释本专利技术,并不构成对本专利技术保护范围的限定。实施例1一种用于电缆的绝缘皮制备配方,按重量份,其原料组成如下:丁苯橡胶64份、氧化锌10份、抗氧剂2份、增塑剂13份、防老化剂8份、充剂135份。抗 ...
【技术保护点】
1.一种用于电缆的绝缘皮制备配方,其特征在于,按重量份,其原料组成如下:
【技术特征摘要】
1.一种用于电缆的绝缘皮制备配方,其特征在于,按重量份,其原料组成如下:所述抗氧剂为为四[甲基-β-(3,5-二叔丁基-4-羟基苯基)丙酸酯]季戊四醇酯;所述增塑剂为52度氯化石蜡和邻苯二甲酸二辛脂的混合物;所述防老化剂为N-异丙基-基对苯二胺;所述填充剂为滑石粉和碳酸钙的混合物。2.如权利要求1所述的一种用于电...
【专利技术属性】
技术研发人员:韦恩明,季成君,
申请(专利权)人:江苏宏鹏电气科技有限公司,
类型:发明