The invention relates to a polymer method of reactive brilliant red K 2BP dye. An amphiphilic compound containing reactive brilliant red group and tertiary amine structure was synthesized, which can be used as initiator for radical polymerization. Its tertiary amine can react with potassium persulfate at room temperature and produce active free radicals for many times. It can initiate both oil-soluble monomer butyl acrylate polymerization and water-soluble monomer Dimethyldiallyl Ammonium Chloride at water/oil interface. Polymerization of reactive brilliant red K_2BP dyes can be achieved by polymerization. This mode can make the functionalization and polymerization non-interfere with each other, operate freely, produce many kinds of products, and the reaction conditions are mild. It does not need organic solvents and emulsifiers, and meets the requirements of green chemistry.
【技术实现步骤摘要】
一种活性艳红染料K-2BP的高分子化方法
本专利技术涉及功能高分子材料合成
，尤其是一种活性艳红染料的高分子化制备技术，通过该新的合成技术可将活性艳红染料分子引入到聚烯烃类高分子材料中，从而产生一类新的功能高分子材料及其相关的应用技术。
技术介绍
聚烯烃是一类非常重要的通用高分子材料，是由若干种烯烃单体通过自由基聚合而形成，针对不同的用途，依据单体共聚合技术实现结构可调，因而应用广泛。引发剂在高分子材料制备中是必不可少的，通常的引发剂是一类能产生自由基的化合物，如油溶性的过氧类、偶氮类引发剂以及水溶性的过硫酸盐等，引发剂的使用必须要与具体的聚合反应环境相配合，传统上认为，一种引发剂只对应某一类的聚合反应，引发剂的结构与功能相对来说比较简单。如果对引发剂的结构和功能进行设计和改造，完全可以使自由基聚合反应发挥出更强的功能，所获得的聚合物材料具有更大的应用价值。活性染料具有反应基团，它可以与纤维上的官能团发生反应，从而将染料分子与材料主体通过化学键连接，使染色更加稳定。活性艳红K-2BP是由H酸与三聚氯氰缩合，再与邻氨基苯磺酸重氮盐偶合，然后与邻氯苯胺缩合而得的...
【技术保护点】
1.一种活性艳红染料的高分子化方法，其特征在于使用如下结构的功能性引发剂：
【技术特征摘要】
1.一种活性艳红染料的高分子化方法，其特征在于使用如下结构的功能性引发剂：所述的高分子化方法的操作步骤依次为：1)将15.0g功能性引发剂分散于800mL水中形成乳化液，浓度控制在1.5～2.0wt.％范围；2)将油溶性丙烯酸丁酯单体加入到乳化液中，单体与引发剂的重量比在1∶1～4∶1范围；充分搅拌后加入过硫酸钾固体粉末，其用量为投入引发剂重量的2.0～3.0％，5～10分钟后聚合反应发生，体系温度有所上升，并很快形成有颜色的聚合物颗粒，聚合反应在1～2小时内完成，...
【专利技术属性】
技术研发人员：李艳，张瑞丰，李赛赛，肖通虎，龙能兵，
申请(专利权)人：宁波大学，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。