The invention discloses a new type of anti-impact agent, whose raw materials are as follows: 20 30 copies of flexible long chain acrylate, 15 26 copies of butadiene, 12 18 copies of vinyl acetate, 10 12 copies of styrene, 5 6 copies of methyl methacrylate, 12 16 copies of diphenyl peroxide, 6 8 copies of terbutyl peroxide. The new type of anti-granulator can replace all the anti-granulator (CPE or CPE+ACR) in the original formula, and its total substitution amount is 50%. The product performance is better than the original formula. Under this dosage, the performance-price ratio of the formula is significantly improved, the cost of the formula is effectively reduced, and the substitution amount of bellows is 40%. The anti-granulator has synergistic effect with calcium stearate, and the total amount of stearic acid used in the original formula is about 40%. Stearic acid in the original formula has better effect.
【技术实现步骤摘要】
一种新型抗冲剂
本专利技术属于PVC抗冲改性剂领域，更具体地说，尤其涉及一种新型抗冲剂。同时，本专利技术还涉及一种新型抗冲剂的制备工艺。
技术介绍
随着我国工业的发展，PVC行业蓬勃发展，但PVC自身的抗冲击性能力差，需加抗冲改性剂。抗冲改性剂主要有ACR、CPE等品种，CPE抗冲改性剂存在冲击强度低，加工范围窄的缺陷，ACR抗冲改性剂具有优良的冲击性能，加工范围宽，但由于我国生产ACR抗冲改性剂的单位研发能力不足，结果使其冲击强度与CPE抗冲改性剂相差不大，由于其生产成本较高，而且使用量较大，不适合推广使用。
技术实现思路
本专利技术的目的在于提供一种新型抗冲剂，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种新型抗冲剂，其原料按重量份如下：丙烯酸柔性长链酯20-30份，丁二烯15-26份，醋酸乙烯酯12-18份，苯乙烯10-12份，甲基丙烯酸甲酯5-6份，过氧化二苯甲酯12-16，过氧化苯甲酸特丁酯6-8份。优选的，所述苯乙烯和甲基丙烯酸甲酯均为界面相容剂，且添加比例为2：1。优选的，所述过氧化二苯甲酯与过氧化苯甲酸特丁酯均为接枝引...
【技术保护点】
1.一种新型抗冲剂，其特征在于，其原料按重量份如下：丙烯酸柔性长链酯20‑30份，丁二烯15‑26份，醋酸乙烯酯12‑18份，苯乙烯10‑12份，甲基丙烯酸甲酯5‑6份，过氧化二苯甲酯12‑16，过氧化苯甲酸特丁酯6‑8份。
【技术特征摘要】
1.一种新型抗冲剂，其特征在于，其原料按重量份如下：丙烯酸柔性长链酯20-30份，丁二烯15-26份，醋酸乙烯酯12-18份，苯乙烯10-12份，甲基丙烯酸甲酯5-6份，过氧化二苯甲酯12-16，过氧化苯甲酸特丁酯6-8份。2.根据权利要求1所述的一种新型抗冲剂，其特征在于：所述苯乙烯和甲基丙烯酸甲酯均为界面相容剂，且添加比例为2：1。3.根据权利要求1所述的一种新型抗冲剂，其特征在于：所述过氧化二苯甲酯与过氧化苯甲酸特丁酯均为接枝引发剂，且添加比例为2：1。4.根据权利要求1所述...