The invention discloses a ready-mixed mortar of machine-made sand concrete, which is made up of 120 140 portions of cement, 220 320 portions of machine-made sand, 60 80 portions of crushed stone, 40 80 portions of fly ash, 3 9 portions of polycarboxylic acid water reducer, 5 11 portions of expansion agent, 0.2 0.8 portions of defoamer, 0.5 1.5 portions of air-entraining agent, 0.2 0.8 portions of coupling agent, 2 4 portions of dispersant and 45 portions of retarder. 55 copies. The invention uses machine-made sand to prepare concrete mixtures, which is beneficial to saving natural resources, solving the problem of shortage of river sand resources, advantageous to environmental protection, having high fluidity, high stability and low slump loss, and fully meeting the construction needs of the construction industry.
【技术实现步骤摘要】
一种机制砂混凝土预拌砂浆
本专利技术涉及一种机制砂混凝土预拌砂浆，属于建筑材料领域。
技术介绍
随着经济建设的飞速发展，我国基础建设方兴未艾，建筑材料消耗巨大。我国预拌砂浆的骨料主要是天然砂，随着建筑面积的不断增加，天然砂的需求量也在不断增加，再加上天然砂的无序开采，导致天然砂资源已经接近枯竭，对环境、生态造成了极大的压力，严重破坏了自然环境。清水混凝土是名副其实的绿色混凝土，混凝土结构不需要装饰，舍去了涂料、饰面等化工产品；有利于环保，清水混凝土结构一次成型，不剔凿修补、不抹灰，减少了大量建筑垃圾，有利于保护环境。目前天然砂资源逐渐枯竭，很多地区机制砂逐渐得到推广，机制砂的应用研究，特别是在各种特殊混凝土中的应用研究，逐渐成为一种趋势。
技术实现思路
本专利技术为解决上述问题，提供了一种机制砂混凝土预拌砂浆。本专利技术实现其目的采用的技术方案为：它是由以下重量份的原料配制而成的：水泥120-140份，机制砂220-320份，碎石60-80份，粉煤灰40-80份，聚羧酸减水剂3-9份，膨胀剂5-11份，消泡剂0.2-0.8份，引气剂0.5-1.5份，偶联剂0.2-0....
【技术保护点】
1.一种机制砂混凝土预拌砂浆，其特征在于，它是由以下重量份的原料配制而成的：水泥120‑140份，机制砂220‑320份，碎石60‑80份，粉煤灰40‑80份，聚羧酸减水剂3‑9份，膨胀剂5‑11份，消泡剂0.2‑0.8份，引气剂0.5‑1.5份，偶联剂0.2‑0.8份，分散剂2‑4份，缓凝剂45‑55份。
【技术特征摘要】
1.一种机制砂混凝土预拌砂浆，其特征在于，它是由以下重量份的原料配制而成的：水泥120-140份，机制砂220-320份，碎石60-80份，粉煤灰40-80份，聚羧酸减水剂3-9份，膨胀剂5-11份，消泡剂0.2-0.8份，引气剂0.5-1.5份，偶联剂0.2-0.8份，分散剂2-4份，缓凝剂45-55份。2.根据权利要求1所述的一种机制砂混凝土预拌砂浆，其特征在于，所述水泥为普通硅酸盐水泥或硅酸盐水泥，其强度等级≥52.3Mpa。3.根据权利要求1所述的一...
【专利技术属性】
技术研发人员：何广振，
申请(专利权)人：徐州金盟新型建材有限公司，
类型：发明
国别省市：江苏,32