The invention discloses a nano-graphene and its preparation method, application and preparation method of solar collector tube. Graphite oxide is prepared by oxidation of graphite with strong acid, potassium permanganate and hydrogen peroxide, and then graphite oxide is prepared by ultrasonic treatment of graphite oxide. Finally, graphene oxide is obtained by reduction with trisodium citrate. The surface is smooth, there are a few folds in the lamellae, and the lamellae are permeable. The graphene prepared by the method has good absorbability, and can be used as absorbent in solar collector tubes.
【技术实现步骤摘要】
一种纳米石墨烯及其制备方法、应用和制备太阳能集热管的方法
本专利技术属于纳米石墨烯的制备应用
，具体涉及一种纳米石墨烯及其制备方法、应用和制备太阳能集热管的方法。
技术介绍
太阳光谱选择性吸收涂层是太阳能光热利用领域的核心材料技术之一。首先，利用纳米材料的优异光热转换性能可有效提高太阳能光热转换效率。在二氧化硅中添加硫化铜可使复合相变材料的光热转换性能得到显著提升。在导热油中添加不同种类和不同质量分数的固体颗粒有助于提高其光热转换特性，石墨-油和铜箔-油显示出良好的光热转换性能。硫化铅/凹凸棒石复合材料的光热转换能力强于体相PbS；对波长300－2500nm的太阳光有比体相PbS更高的吸收率；复合材料中的PbS比体相PbS的电子跃迁能带更宽；材料密度远低于体相PbS，可以在同等厚度下覆盖更大的面积。然而，纳米材料吸光率对太阳能集热管光热转换作用的研究鲜有公开报道。
技术实现思路
本专利技术的目的在于提供一种纳米石墨烯及其制备方法、应用和制备太阳能集热管的方法，制备的纳米石墨烯具有良好的吸光性能，可作为吸光剂应用在太阳能集热管上。本专利技术是通过以下技术方案来实现...
【技术保护点】
1.一种纳米石墨烯的制备方法，其特征在于，包括以下步骤：1)在冰水浴的条件下，将硫酸和磷酸以玻璃棒引流的方式与石墨粉混合，控制反应温度在0～4℃，持续搅拌反应1～2h；其中，硫酸与磷酸的质量比为9：1；2)向步骤1)制得的混合溶液加入高锰酸钾，控制反应温度在0～7℃，边加边搅拌，持续搅拌1～2h，后升温至35～40℃，持续搅拌0.5～1h；其中，石墨粉与高锰酸钾的质量比为1：3；3)向步骤2)制得的混合溶液中滴入去离子水，将温度升至85～98℃，持续反应1～2h后，加入双氧水，这时烧杯中会有金黄色出现，即为氧化石墨溶液；4)对步骤3)制得的氧化石墨溶液进行洗涤离心，直至溶液...
【技术特征摘要】
1.一种纳米石墨烯的制备方法，其特征在于，包括以下步骤：1)在冰水浴的条件下，将硫酸和磷酸以玻璃棒引流的方式与石墨粉混合，控制反应温度在0～4℃，持续搅拌反应1～2h；其中，硫酸与磷酸的质量比为9：1；2)向步骤1)制得的混合溶液加入高锰酸钾，控制反应温度在0～7℃，边加边搅拌，持续搅拌1～2h，后升温至35～40℃，持续搅拌0.5～1h；其中，石墨粉与高锰酸钾的质量比为1：3；3)向步骤2)制得的混合溶液中滴入去离子水，将温度升至85～98℃，持续反应1～2h后，加入双氧水，这时烧杯中会有金黄色出现，即为氧化石墨溶液；4)对步骤3)制得的氧化石墨溶液进行洗涤离心，直至溶液呈中性，后将沉淀物取出，蒸发干燥，获得氧化石墨粉；5)将制得的氧化石墨粉制成氧化石墨溶液，超声处理后，得到氧化石墨烯溶液；6)向氧化石墨烯溶液中加入柠檬酸三钠，升温至80～90℃，搅拌反应5～6.5h，将得到的产物洗涤离心，直至离心得到的上清液pH达到中性；最后将沉淀物...