The invention discloses a preparation method of ultra-fine grained magnesium alloy extruded bar. In the process of hot extrusion preparation of magnesium alloy bar, the extruded magnesium alloy is twisted synchronously, which causes severe deformation under the combined stress field formed by tension stress and torsion stress, effectively fines the structure of magnesium alloy and improves the comprehensive mechanical properties of wrought magnesium alloy. This method realizes the goal of grain refinement by conventional process and develops low cost and high performance wrought magnesium alloy. It can make full use of simple equipment to produce wrought magnesium alloy products, effectively shorten the preparation process, save energy, reduce costs, and is easy to popularize and apply.
【技术实现步骤摘要】
一种超细晶镁合金挤压棒材的制备方法
本专利技术涉及变形镁合金的制备方法，尤其涉及一种超细晶镁合金挤压棒材的制备方法，属于镁合金加工
技术介绍
镁合金作为最轻的金属结构材料，具有比强度高，散热性能和阻尼性能好、环境友好等优点，已成为最具发展潜力的金属结构材料之一。但是,镁合金具有密排六方晶体结构,具有的独立滑移系较少,室温变形能力较差；而且,镁合金在塑性变形过程中极易产生孪生变形,导致屈服强度低和拉压屈服不对称等，这些缺点都严重限制了镁合金的广泛使用。析出强化、加工硬化等可以显著提高绝对强度，但同时又进一步损害塑性。如何在提高强度的同时提高塑性是国内外镁合金发展的重点之一。晶粒细化已证明是一种能同时提高强度和塑性的重要手段。当晶粒细化至数个微米量级时，变形过程中能够大量激活晶界滑移，协调变形，因此不仅可提高镁合金的强度还能显著改善合金的塑性。超细晶材料通常指晶粒尺寸~1μm的材料。在超细晶钢中，一般认为超细晶组织的目标是将晶粒尺寸从传统的几十微米大小细化至一个数量级，达到1μm~2μm的组织。在钢铁材料中，利用超细晶组织可使材料性能加倍。近期研究表明，超细...
【技术保护点】
1.一种超细晶镁合金挤压棒材的制备方法，其特征在于，在热挤压制备镁合金棒材的过程中，挤压镁合金时同步对其进行扭转，使其在受拉应力与扭转应力形成的复合应力场的作用下产生变形。
【技术特征摘要】
1.一种超细晶镁合金挤压棒材的制备方法，其特征在于，在热挤压制备镁合金棒材的过程中，挤压镁合金时同步对其进行扭转，使其在受拉应力与扭转应力形成的复合应力场的作用下产生变形。2.根据权利要求1所述超细晶镁合金挤压棒材的制备方法，其特征在于，具体包括以下步骤：启动挤压装置，在200℃~500℃的条件下，挤压杆以0.1~10m/min的挤压速度挤压镁合金铸锭或铸态铸锭，同时以挤压方向为轴利用牵引设备对所述镁合金铸锭或铸态铸锭进行扭转，扭转速度为0.1~80r/s，使所其产生变形，获得超细晶镁合金挤压棒材。3.根据权利要求2所述超细晶镁合金挤压棒材的制备方法，其特征在于，所述镁合金铸锭或铸态铸锭在挤压前需要进行热处理；所述热处理为固溶热处理、T5峰值时效热处理和T6峰值时效热处理中的一种...
【专利技术属性】
技术研发人员：潘复生，佘加，彭鹏，汤爱涛，蒋斌，
申请(专利权)人：重庆大学，
类型：发明
国别省市：重庆,50
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。