一种超薄的RhPdH纳米片材料及其制备方法与应用技术

本发明专利技术公开了一种超薄的RhPdH纳米片的制备及其在电催化析氢方面的应用。RhPdH纳米片的尺寸范围为200～325nm，其厚度范围为1.5～2nm。该材料通过一步溶剂热法成功制备，Rh(acac)3和Pd(acac)2为前驱体盐，甲醛为溶剂，聚乙烯吡咯烷酮为表面覆盖剂，并在此基础上引入CO气体，得到了纯净的超薄RhPdH纳米片结构。并对其进行了电催化析氢性能的研究，RhPdH纳米片表现出优良的电催化析氢性能，同时表现了超高的电催化析氢稳定性。

A Thin RhPdH Nanosheet Material and Its Preparation Method and Application

The invention discloses the preparation of an ultra-thin RhPdH nanosheet and its application in electrocatalytic hydrogen evolution. RhPdH nanosheets are 200-325 nm in size and 1.5-2 nm in thickness. Rh (acac) 3 and Pd (acac) 2 were used as precursor salts, formaldehyde as solvent and polyvinylpyrrolidone as surface covering agent. On this basis, CO gas was introduced to obtain pure ultra-thin RhPdH nanosheets. The electrocatalytic hydrogen evolution performance of RhPdH nanosheets was studied. RhPdH nanosheets exhibited excellent electrocatalytic hydrogen evolution performance and super high electrocatalytic hydrogen evolution stability.

【技术实现步骤摘要】
一种超薄的RhPdH纳米片材料及其制备方法与应用
本专利技术属于清洁可持续新型能源制备应用领域，特别涉及一种超薄的RhPdH纳米片材料及其制备方法与应用。
技术介绍
贵金属不同晶面对于催化活性的影响巨大，使高催化活性的晶面裸露在外成为研究的热点，于是贵金属的形貌调控应运而生。比如，当裸露晶面是(111)面时，往往呈现四面体或八面体的形貌，当(100)晶面裸露在外时呈现的是立方体的形貌。正是由于不同的裸露晶面构筑了贵金属纳米材料千姿百态的形貌。经过几十年的发展与进步，在贵金属以及非贵金属的形貌调控方面取得了巨大的突破，一维的纳米棒，纳米线，二维的纳米片，纳米盘，三维的纳米立方体、四面体、截角八面体等形貌被成功地制备出来，使得这个大家族逐渐丰富。二维材料由于具有高的电子迁移率、量子霍尔效应、优良的热导率以及超导性能，成为形貌调控的重点，受到研究者的广泛关注。人们又将二维材料分为层状二维材料和非层状二维材料，层状二维材料包括石墨烯、六方氮化硼、黑磷、MOFs、COFs、MXenes、MoS2等，它们具有强的层内化学键和弱的层间范德华键，具有轻微的晶格扭曲，而非层状二维材料主要包括金属及其合本文档来自技高网...

【技术保护点】
1.一种超薄的RhPdH纳米片电催化析氢材料，其特征在于，Rh、Pd、H三元素组成面心立方的合金结构，纳米片尺寸范围为200～325nm，厚度范围为1.5～2nm。

【技术特征摘要】
1.一种超薄的RhPdH纳米片电催化析氢材料，其特征在于，Rh、Pd、H三元素组成面心立方的合金结构，纳米片尺寸范围为200～325nm，厚度范围为1.5～2nm。2.一种权利要求1所述材料的制备方法，其特征在于，包括以下步骤：(1)称取前驱体盐Rh(acac)3和Pd(acac)2各6～10mg溶解在5～10mL的甲醛溶剂中，同时加入聚乙烯吡咯烷酮110～130mg，...

【专利技术属性】
技术研发人员：崔小强，武建栋，范锦昌，刘畅，
申请(专利权)人：吉林大学，
类型：发明
国别省市：吉林,22