The invention discloses a preparation method of Phenolamine coated iron oxide material for removing dye ions. The material comprises tannic acid (TA), hexanediamine (HA) and iron oxide. The preparation steps of the material are as follows: firstly dissolve ferric chloride in water and add a certain amount of sodium hydroxide to make it precipitate, then separate and redisperse the precipitate in ultra-pure water, then add a certain amount of tannic acid, finally add hexanediamine, centrifugal drying to make Phenolamine coated iron oxide material. The adsorbent material prepared by the invention has good stability, simple preparation process, strong operability, low cost, recyclable utilization and no secondary pollution, and is widely used in the field of removing dye ions from sewage.
【技术实现步骤摘要】
一种去除染料离子的酚胺包覆铁氧化物材料的制备方法
本专利技术涉及吸附剂的制备，具体涉及一种去除染料离子的酚胺包覆铁氧化物材料的制备方法。
技术介绍
随着科技的发展和工业的进步，化工产业不断发展，越来越多的化工产品随之进入到我们的生活中给我们带来了极大的方便。然而，当人们沉浸在化工产品带来的便捷中时，环境问题也变得日益突出，人类面临工业化带来的极大负面效果，比如生态污染、能源紧缺、资源枯竭，特别是水资源的浪费与污染。其中，水污染问题的产生因素之一就是染料离子污染，虽然水溶性染料具有低的光学稳定性、氧化性能，但是它们仍然很难在环境中降解。由于环境中的污染物含有大量的毒性物质，近年来受到人们的普遍关注，尤其是排放废水的有机染料。这些毒性染料主要来源于为使用染料颜色产品的工厂，如纺织、造纸、染料、塑料等行业，很容易随自然循环而发生扩散。大多数染料具有非生物降解性和致癌的作用，能通过饮用水进入生物体内，直接破坏人体的正常器官组织，危害生物体的健康安全。因此，一旦大量的染料分子积累在环境中，长期的毒性危害不容忽视。例如，染料的存在阻碍了水的饮用质量，并且会减少在水生生态系统中...
【技术保护点】
1.一种去除染料离子的酚胺包覆铁氧化物材料的制备方法，其特征在于以下步骤：（1）在室温条件下，将一定质量的氯化铁分散到超纯水中并加入适量的氢氧化钠，使其出现沉淀。（2）将上述沉淀重新分散到水中，然后加入一定量的单宁酸，并搅拌12～36h。（3）向上述步骤（2）的溶液中加入一定量的己二胺，并搅拌24～72h，最后离心并用去离子水冲洗2～4次，冷冻干燥，即可制得酚胺包覆铁氧化物材料。
【技术特征摘要】
1.一种去除染料离子的酚胺包覆铁氧化物材料的制备方法，其特征在于以下步骤：（1）在室温条件下，将一定质量的氯化铁分散到超纯水中并加入适量的氢氧化钠，使其出现沉淀。（2）将上述沉淀重新分散到水中，然后加入一定量的单宁酸，并搅拌12～36h。（3）向上述步骤（2）的溶液中加入一定量的己二胺，并搅拌24～72h，最后离心并用去离子水冲洗2～4次，冷冻干燥，即可制得酚胺包覆铁氧化物材料。2...
【专利技术属性】
技术研发人员：刘钦泽，高嵩，刘鹏，张文丽，张艳，胡涛，
申请(专利权)人：齐鲁工业大学，
类型：发明
国别省市：山东,37