The utility model discloses a single silver low radiation film glass with low color difference after tempering, which comprises a glass base. The top surface of the glass base is successively stacked with the first silicon nitride layer, the first nickel chromium layer, the silver layer, the second nickel chromium layer and the second silicon nitride layer from bottom to top; the thickness of the first silicon nitride layer is 15-35 nm, and the thickness of the first nickel chromium layer. The thickness of the silver layer is 9-15 nm, the thickness of the second nickel-chromium layer is 1.5-5 nm, and the thickness of the second silicon nitride layer is 45-60 nm. The products before and after tempering can be mixed for the same project; the utility model can be prepared by using conventional target materials and magnetron sputtering process, with low cost, controllable process and high stability.
【技术实现步骤摘要】
一种钢化后低颜色差异的单银低辐射膜玻璃
本技术涉及功能玻璃
，具体是一种钢化后低颜色差异的单银低辐射膜玻璃。
技术介绍
单银低辐射镀膜玻璃，又称LOW-E玻璃，是指在普通玻璃表面通过磁控溅射的方法沉积多层非金属膜与一层金属膜，金属层材料通常选用银，银层作为功能层对红外线有着较高的反射作用，从而起到了一定的隔热保温作用，达到节能损耗的效果。低辐射镀膜玻璃已普遍应用于建筑及汽车玻璃行业，市面上多数单银低辐射镀膜玻璃几乎都是可钢化产品，但钢化后玻璃面反射色与钢化前差异较大，肉眼可明显区分出颜色差异，不能满足行业需要。
技术实现思路
本技术的目的在于提供一种钢化后低颜色差异的单银低辐射膜玻璃，该玻璃在钢化前与钢化后的颜色差异小，满足工程建设的需求。本技术解决其技术问题所采用的技术方案是：一种钢化后低颜色差异的单银低辐射膜玻璃，包括玻璃基底，玻璃基底顶面由下至上依次层叠有第一氮化硅层、第一镍铬层、银层、第二镍铬层与第二氮化硅层；所述第一氮化硅层的厚度为15～35nm、第一镍铬层的厚度为1.5～3nm、银层的厚度为9～15nm、第二镍铬层的厚度为1.5～5nm、第二氮化硅层的厚...
【技术保护点】
1.一种钢化后低颜色差异的单银低辐射膜玻璃，其特征在于，包括玻璃基底，玻璃基底顶面由下至上依次层叠有第一氮化硅层、第一镍铬层、银层、第二镍铬层与第二氮化硅层；所述第一氮化硅层的厚度为15～35nm、第一镍铬层的厚度为1.5～3nm、银层的厚度为9～15nm、第二镍铬层的厚度为1.5～5nm、第二氮化硅层的厚度为45～60nm。
【技术特征摘要】
1.一种钢化后低颜色差异的单银低辐射膜玻璃，其特征在于，包括玻璃基底，玻璃基底顶面由下至上依次层叠有第一氮化硅层、第一镍铬层、银层、第二镍铬层与第二氮化硅层；所述第...
【专利技术属性】
技术研发人员：张山山，李险峰，沈晓晨，邱宏，罗雨潇，刘云南，
申请(专利权)人：中建材光电装备太仓有限公司，
类型：新型
国别省市：江苏,32