The invention discloses a rapid method for determining the true density of powder, which uses density balance to determine the true density of powder, in particular, first pouring degassed leaching solution into the liquid tank of electronic balance, then adding appropriate dispersant to obtain the density of leaching solution, and then placing equal-sized filter membrane on weighing net to make the filter membrane. Immersed in the leaching solution and without touching with the liquid tank, peeled after the stability of the indicator number; then added the dry powder called M1, slightly stirred to remove the bubbles in it, and read out the mass M2 after the indicator number is stable; finally, the true density of powder can be obtained by using the formula [1/M1 M2] Rho solution. The method has the advantages of convenient use, simple operation, accurate measurement value and rapid determination of true density of powder.
【技术实现步骤摘要】
一种快速测定粉体真密度的方法
本专利技术涉及粉体密度测定领域,具体涉及一种快速测定粉体真密度的方法。
技术介绍
粉体真密度是粉体质量与其真体积之比值,其真体积不包括存在于粉体颗粒内部的封闭空洞。所以,测定粉体的真密度必须采用无孔材料。根据测定介质的不同,粉体真密度的主要测定方法可分为气体容积法和浸液法。气体容积法是以气体取代液体测定试样所排出的体积。此法排除了浸液法对试样溶解的可能性,具有不损坏试样的优点,但测定时易受温度的影响,还需注意漏气问题。浸液法是将粉末浸入在易润湿颗粒表面的浸液中,测定其所排除液体的体积。此法必须真空脱气以完全排除气泡。真空脱气操作可采用加热(煮沸)法和减压法,或两法同时并用,操作较为繁琐。
技术实现思路
为解决上述问题,本专利技术提供了一种更科学的、更简单的、更方便的,更快速的测定粉体真密度的方法。为实现上述目的,本专利技术采取的技术方案为:一种快速测定粉体真密度的方法,利用密度天平测定粉体的真密度,包括如下步骤:S1、取制备好的粉体进行干燥,称取质量为M1的干燥粉体;S2、取适量的浸液倒入烧杯中,再将烧杯置于真空干燥器内进行预先脱气,计算浸液的密度ρ液;S3、将脱气后的浸液倒入电子天平的液体槽中,浸液的体积为液体槽体积的2/3,再加入适量的分散剂,使粉体快速分散在溶剂中;S4、在称量网上放置大小相等的滤膜,使得滤膜浸没在浸液中,并与液体槽不发生触碰,待示数稳定后,去皮;再加入所称取的干燥粉体,轻微的搅拌排除其中的气泡,待示数稳定后读出质量M2;S5、根据阿基米德原理可知,M1-ρ液gV=M2g;ρ真=M1/V,因此,可以得到:ρ真 ...
【技术保护点】
1.一种快速测定粉体真密度的方法,其特征在于:利用密度天平测定粉体的真密度。
【技术特征摘要】
1.一种快速测定粉体真密度的方法,其特征在于:利用密度天平测定粉体的真密度。2.如权利要求1所述的一种快速测定粉体真密度的方法,其特征在于:包括如下步骤:S1、取制备好的粉体进行干燥,称取质量为M1的干燥粉体;S2、取适量的浸液倒入烧杯中,再将烧杯置于真空干燥器内进行预先脱气,计算浸液的密度ρ液;S3、将脱气后的浸液倒入电子天...