The present invention relates to a preparation method of aminopyridine functionalized magnetic Fe3O4 metal ion adsorbent, which includes: firstly, aminopyridine was modified to 3(2,3)propylene trimethoxysilane by 2_aminopyridine to obtain aminopyridine functionalized silane coupling agent, and then the magnetic nanometer Fe3O4 coated with silica was obtained by this method. The adsorbent was obtained by functionalization. The adsorbent prepared by the invention has the advantages of simple preparation process, high content of functional groups, good adsorption performance, good adsorption selectivity and easy separation, and can be widely used in the fields of adsorption, separation and enrichment of heavy metal ions in water.
【技术实现步骤摘要】
一种氨基吡啶功能化磁性Fe3O4金属离子吸附剂的制备方法
本专利技术涉及一种氨基吡啶功能化磁性Fe3O4金属离子吸附剂的制备方法，属于环境功能材料领域。
技术介绍
随着工业化的不断发展，电子、冶金、印染等领域的排污量急剧增加，其中含重金属离子的废水所导致的环境问题受到人们越来越多的关注。重金属离子在环境中难以被生物降解且进入人体后会不断富集，对人体造成伤害。因此有效脱除环境中的重金属离子具有重要意义。传统的治理方法包括化学沉淀法、离子交换法、电解法、吸附法等，吸附法由于成本低、操作简单、吸附效果显著等优点被广泛应用。制备经济高效、操作方便、性能稳定的金属离子吸附剂是吸附法的关键。磁性纳米Fe3O4具有制备工艺简单、比表面积大、易于表面修饰、容易磁分离等优点成为研究的热点。但磁性纳米Fe3O4易团聚、吸附性能和吸附选择性差，因此，通常对其进行功能化以克服上述缺点。采用二氧化硅对磁性纳米Fe3O4进行包覆并进一步功能化是常用的方法。二氧化硅具有良好的机械性能、热力学和化学稳定性、表面富含硅羟基易于进行功能化等优点。氨基吡啶含有氮、氧原子，已被证明对重金属离子具有良好的...
【技术保护点】
1.一种氨基吡啶功能化磁性Fe3O4金属离子吸附剂的制备方法，其特征在于，包括：以无水乙醇为溶剂，取2‑氨基吡啶与3‑(2,3‑环氧丙氧)丙基三甲氧基硅烷加热搅拌反应，随后加入二氧化硅包覆磁性纳米Fe3O4和甲苯，超声分散、反应，反应结束后通过磁铁进行分离，然后用无水乙醇回流萃取至少12小时，最后干燥得到氨基吡啶功能化磁性纳米Fe3O4金属离子吸附剂。
【技术特征摘要】
1.一种氨基吡啶功能化磁性Fe3O4金属离子吸附剂的制备方法，其特征在于，包括：以无水乙醇为溶剂，取2-氨基吡啶与3-(2,3-环氧丙氧)丙基三甲氧基硅烷加热搅拌反应，随后加入二氧化硅包覆磁性纳米Fe3O4和甲苯，超声分散、反应，反应结束后通过磁铁进行分离，然后用无水乙醇回流萃取至少12小时，最后干燥得到氨基吡啶功能化磁性纳米Fe3O4金属离子吸附剂。2.根据权利要求1所述的制备方法，其特征在于，...
【专利技术属性】
技术研发人员：牛余忠，张在鑫，陈厚，任冰，
申请(专利权)人：鲁东大学，
类型：发明
国别省市：山东,37