A method for preparing aromatic monomers by lignin dioxide degradation includes the following steps: suspending lignin, oxidant and inorganic acid in molten salt mixture according to mass ratio, stirring evenly, and reacting at 90-150 (?) C for 0.5-5 h; draining and washing 3-4 times after the reaction liquid is cooled, and then placing them in 20 mL hydrogen peroxide water. The lignin monomer compounds can be obtained by vacuum drying after ethyl acetate extracting and degrading the products, rotating evaporation removing organic solvents. The method has mild reaction conditions, fast and efficient reaction, and can effectively degrade lignin by breaking the ether bond (beta_O_4) and carbon-carbon bond (Calpha_Cbet); furthermore, the highest yield of lignin monomer compounds is up to 80%.
【技术实现步骤摘要】
一种木质素双氧化降解制备芳香单体的方法
本专利技术属于木质素转化
，具体涉及一种木质素双氧化降解制备芳香单体的方法。
技术介绍
由于化石燃料短缺和环境问题日益加剧，木质纤维素生物质被认为是液体燃料和化学品生产的潜在原料和可持续资源。在过去十年中，由木质纤维素生物质源（纤维素和半纤维素）转化碳水化合物已经实现了重大突破，例如开发第二代生物燃料（纤维素转化制备生物乙醇））和生物基化学物质（乳酸，琥珀酸，乙酰丙酸及其衍生物等）[Kloekhorst,A.;Heeres,H.J.ACSSustainableChem.Eng.2015,3,1905−1914]。然而，因为木质素结构的复杂性、大分子的多分散性以及物理化学性质的不均一性，作为继纤维素后的第二大天然聚合物木质素却仍未获有效利用。因此，开发有效的木质素转化方法已成为目前的研究热点[Ragauskas,A.J.;Beckham,G.T.;Biddy,M.J.;Chandra,R.;Chen,F.;Davis,M.F.;Davison,B.H.;Dixon,R.A.;Gilna,P.;Keller,M.;Lang...
【技术保护点】
1.一种木质素双氧化降解制备芳香单体的方法，其特征在于步骤为：按比例，把2 g木质素和0.2～2.0 g的氧化剂悬浮于20 mL熔盐水合物中搅拌均匀，加入50～200 μL的无机酸，在90～150 ℃下反应0.5～5 h；待反应液冷却至室温后，抽滤，水洗产物3～4次；再将产物置于20 mL双氧水中，20～80 ℃反应5～24 h，待反应液冷却至室温后，乙酸乙酯萃取降解产品，旋转蒸发除去有机溶剂，真空干燥可得木质素单体化合物。
【技术特征摘要】
1.一种木质素双氧化降解制备芳香单体的方法，其特征在于步骤为：按比例，把2g木质素和0.2～2.0g的氧化剂悬浮于20mL熔盐水合物中搅拌均匀，加入50～200μL的无机酸，在90～150℃下反应0.5～5h；待反应液冷却至室温后，抽滤，水洗产物3～4次；再将产物置于20mL双氧水中，20～80℃反应5～24h，待反应液冷却至室温后，乙酸乙酯萃取降解产品，旋转蒸发除去有机溶剂，真空干燥可得木质素单体化合物。2.根据权利要求1所述木质素双氧化降解制备芳香单体的方法，其特征在于所述木质素为Kraft木质素、有机溶剂型木质素或酶解木...
【专利技术属性】
技术研发人员：杨晓慧，景菲，周永红，博采颖，尚倩倩，
申请(专利权)人：中国林业科学研究院林产化学工业研究所，
类型：发明
国别省市：江苏,32