The application of the invention discloses a coated sand, including aggregate, resin and curing agent, and also an arbitrary proportion mixture of one or more components of organic grease with viscosity less than 1000cp. According to the mass ratio, the amount of added organic grease is less than 0.008% of the aggregate weight. The application of the invention also discloses the coated sand mentioned above. The preparation method. The coated sand prepared by the invention not only greatly reduces the dust in the blowing and dumping process, but also improves the fluidity, improves the hydrophilicity of the coated sand and the anti-adhesion and caking between particles in the storage process of the coated sand, makes the prepared sand core more compact, and improves the core-making efficiency.
【技术实现步骤摘要】
一种覆膜砂及其制备方法
本专利技术属于铸造造型
，具体涉及一种覆膜砂及其制备方法。
技术介绍
覆膜砂(resincoatedsand),是砂粒表面在造型前即覆有一层固体树脂膜的型砂或芯砂。有冷法和热法两种覆膜工艺：冷法用乙醇或丙酮等有机类溶剂将树脂溶解，并在混砂过程中加入乌洛托品，使二者包覆在砂粒表面，乙醇或丙酮等有机类溶剂挥发，得覆膜砂；热法把砂预热到一定温度，加树脂使其熔融，搅拌使树脂包覆在砂粒表面，加乌洛托品水溶液及润滑剂，冷却、破碎、筛分得覆膜砂。覆膜砂主要采用优质精选天然石英砂为原砂，热塑性酚醛树脂，乌洛托品及增强剂为原料。根据用户的不同技术需求，在固化速度、脱膜性、流动性、溃散性、铸件表面光洁度、储存等方面适当调整配比，是汽车、拖拉机、液压件等最佳造型材料之一。现有的覆膜砂在应用过程中，在倾倒、吹送、制芯等工艺过程中会产生大量的粉尘，从而导致作业环境恶劣，同时覆膜砂产品属于型砂制造者在应用前需要一定的储存过程，在储存过程中受到仓容的限制或为了提高仓库使用效果，常常会将装有覆膜砂的包装袋堆码存放，因此在环境温度、湿度、堆码高度等情况不同造成覆膜砂颗...
【技术保护点】
1.一种覆膜砂，包括骨料、树脂和固化剂，其特征在于，还包括粘度在1000cp以下的有机油脂的单一组分或多种组分的任意比例混合物，按质量比，所述有机油脂的添加量为骨料重的0.008％以下。
【技术特征摘要】
1.一种覆膜砂，包括骨料、树脂和固化剂，其特征在于，还包括粘度在1000cp以下的有机油脂的单一组分或多种组分的任意比例混合物，按质量比，所述有机油脂的添加量为骨料重的0.008％以下。2.根据权利要求1所述的一种覆膜砂，其特征在于，所述有机油脂为硅油、色拉油或者菜籽油。3.根据权利要求1所述的一种覆膜砂，其特征在于，所述有机油脂的的粘度为500-1000cp。4.根据权利要求1或2所述的一种覆膜砂，其特征在于，所述有机油脂为硅油，所述硅油的添加量为骨料重的0.0007-0.002％。5.根据权利要求4所述的一种覆膜砂，其特征在于，所述硅油采用甲基硅油。6.根据权利要求1所述的一种覆膜砂，其特征在于，所述树脂为热塑性的树脂。7.根据权利要求1所述的一种覆膜砂，其特征在于，还包括隔离剂，所述隔离剂占骨料、树脂和固化剂总重的1-2‰。8.一种覆膜砂的制备方法，其特征在于，包括以下制备步骤...
【专利技术属性】
技术研发人员：熊鹰，熊帆，王丽峰，蔡颖，孙伟民，
申请(专利权)人：重庆长江造型材料集团股份有限公司，
类型：发明
国别省市：重庆,50
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。