The invention discloses a water-resistant submarine photovoltaic cable sheath material, which comprises 30_40 copies of nitrile silicone rubber, 10_20 copies of fluorosilicone rubber, 30_60 copies of acrylate rubber, 4_6 copies of crosslinking agent, 1_2 copies of polyvinyl butyral, 75_95 copies of filler, 2_4 copies of plasticizer, 1_2 copies of disproportionated rosin, 1_2 cope of antioxidant. 2 copies. The crosslinking agent by weight includes 1.2 2 parts of sodium dichromate, 2 8 parts of N, N nitrobisacrylamide and 0.2 0.8 parts of diisopropylbenzene peroxide. The submarine photovoltaic cable sheath material of the invention has high crosslinking density, excellent wear resistance and toughness, excellent waterproof effect, and excellent ageing resistance even if it is immersed in seawater for a long time.
【技术实现步骤摘要】
一种耐水海底光伏电缆护套材料
本专利技术涉及电缆
,尤其涉及一种耐水海底光伏电缆护套材料。
技术介绍
近些年,国内光伏电缆有较快发展,国内许多企业已具备一定的光伏电缆生产技术,适用于普通场所的光伏电缆国内技术已经可以达到要求。但在一些苛刻条件下,尤其是电缆护套长期浸泡在海水中,电缆的外护层易发生渗透甚至开裂,所以无法满足海水浸泡环境的使用。而普通电缆要达到性要求要从电缆结构上进行改进,如增加耐水防护层,此举大大增加电缆的制作成本及使用成本,不适宜推广。
技术实现思路
基于
技术介绍
存在的技术问题,本专利技术提出了一种耐水海底光伏电缆护套材料,交联密度高,耐磨和韧性极好,防水效果极好,即使长期浸泡在海水中仍不易开裂,耐老化性能优异。本专利技术提出的一种耐水海底光伏电缆护套材料,其料按重量份包括:腈硅橡胶30-40份,氟硅橡胶10-20份,丙烯酸酯橡胶30-60份,交联剂4-6份,聚乙烯醇缩丁醛1-2份,填充剂75-95份,增塑剂2-4份,歧化松香1-2份,防老剂1-2份。优选地,交联剂按重量份包括:重铬酸钠1.2-2份,N,N-亚硝基双丙烯酰胺2-8份,过氧化二异丙苯0.2-0.8份。优选地,填充剂按重量份包括:煅烧高岭土20-40份,滑石粉50-80份,丙烯腈基碳纤维3-14份。优选地,增塑剂按重量份包括:氧化聚乙烯蜡1-2份,端乙烯基硅油1-2份。优选地,防老剂按重量份包括:抗氧剂AT-2150.2-1份,紫外光吸收剂UV-5310.2-0.4份,紫外光吸收剂TB750.1-0.2份。本专利技术采用腈硅橡胶与氟硅橡胶、丙烯酸酯橡胶复配,在端乙烯基硅油的配 ...
【技术保护点】
1.一种耐水海底光伏电缆护套材料,其特征在于,其料按重量份包括:腈硅橡胶30‑40份,氟硅橡胶10‑20份,丙烯酸酯橡胶30‑60份,交联剂4‑6份,聚乙烯醇缩丁醛1‑2份,填充剂75‑95份,增塑剂2‑4份,歧化松香1‑2份,防老剂1‑2份。
【技术特征摘要】
1.一种耐水海底光伏电缆护套材料,其特征在于,其料按重量份包括:腈硅橡胶30-40份,氟硅橡胶10-20份,丙烯酸酯橡胶30-60份,交联剂4-6份,聚乙烯醇缩丁醛1-2份,填充剂75-95份,增塑剂2-4份,歧化松香1-2份,防老剂1-2份。2.根据权利要求1所述耐水海底光伏电缆护套材料,其特征在于,交联剂按重量份包括:重铬酸钠1.2-2份,N,N-亚硝基双丙烯酰胺2-8份,过氧化二异丙苯0.2-0.8份。3.根据权利要求1或2所述耐水海底光伏...
【专利技术属性】
技术研发人员:巫春生,张家文,徐志敏,
申请(专利权)人:安徽渡江电缆集团有限公司,
类型:发明
国别省市:安徽,34