The preparation method of the polysilicone flue gas anticorrosive coating provided by the invention is that the resin mixture is obtained by stirring the polysilicone modified epoxy resin, titanium dioxide and mica powder; the resin mixture, nano-silica powder, graphite and nano-zinc oxide are mixed and stirred to obtain component A; and the polysilicon is obtained by mixing the component A with the curing agent. The flue gas anticorrosive coating, the polysilicon flue gas anticorrosive coating obtained by the above-mentioned preparation method, uses the inorganic-organic interpenetrating network polymer as the film forming material, has the properties of high temperature resistance, acid-alkali corrosion resistance, heat shock resistance, wear resistance and dust erosion resistance.
【技术实现步骤摘要】
聚硅烟气防腐涂料及其制备方法
本专利技术涉及防腐涂料
，特别是涉及一种聚硅烟气防腐涂料及其制备方法。
技术介绍
烟气温度一般在70℃-500℃，流速一般都在5m/s以上，粉尘颗粒物粒径大小在0.3毫米以上，粉尘浓度在10％以上，相对湿度为3-10％，含有灰分及各种腐蚀性成分，如SO2、NO2、HCl、盐雾等，甚至有的烟气中含有氢氟酸强腐蚀气体存在，造成酸碱腐蚀。低温烟气在烟囱内结露形成冷凝酸液，对烟囱材料的腐蚀也比较严重。因此，烟气防腐要求的防腐条件比较苛刻。为了解决湿烟囱的防腐问题，必须寻求一种耐酸防腐、耐温变强、耐高温同时耐磨附着力又好的材料。
技术实现思路
基于此，有必要针对现有技术中存在的缺陷，提供一种防腐性能好的聚硅烟气防腐涂料。为实现上述目的，本专利技术采用下述技术方案：一种聚硅烟气防腐涂料的制备方法，包括下述步骤：将聚硅烷改性环氧树脂、钛白粉及云母粉搅拌后得到树脂混合物；将所述树脂混合物、纳米硅微粉、石墨及纳米氧化锌混合搅拌后得到组分A；及将所述组分A与固化剂混合得到所述聚硅烟气防腐涂料。在一些较佳实施例中，在将聚硅烷改性环氧树脂、钛白粉及云母粉搅...
【技术保护点】
1.一种聚硅烟气防腐涂料的制备方法，其特征在于，包括下述步骤：将聚硅烷改性环氧树脂、钛白粉及云母粉搅拌后得到树脂混合物；将所述树脂混合物、纳米硅微粉、石墨及纳米氧化锌混合搅拌后得到组分A；及将所述组分A与固化剂混合得到所述聚硅烟气防腐涂料。
【技术特征摘要】
1.一种聚硅烟气防腐涂料的制备方法，其特征在于，包括下述步骤：将聚硅烷改性环氧树脂、钛白粉及云母粉搅拌后得到树脂混合物；将所述树脂混合物、纳米硅微粉、石墨及纳米氧化锌混合搅拌后得到组分A；及将所述组分A与固化剂混合得到所述聚硅烟气防腐涂料。2.根据权利要求1所述的聚硅烟气防腐涂料的制备方法，其特征在于，在将聚硅烷改性环氧树脂、钛白粉及云母粉搅拌后得到树脂混合物的步骤中，所述聚硅烷改性环氧树脂通过下述方法制备：将硅烷KH-550与环氧树脂混合搅拌，形成聚硅烷改性环氧树脂。3.根据权利要求2所述的聚硅烟气防腐涂料的制备方法，其特征在于，所述硅烷与环氧树脂的体积比为1：10-1：15。4.根据权利要求2所述的聚硅烟气防腐涂料的制备方法，其特征在于，在将聚硅烷改性环氧树脂、钛白粉及云母粉搅拌后得到树脂混合物的步骤中，所述钛白粉、所述云母粉和所述聚硅烷改性环氧树脂的质量比为1：2：1-1：4：2。5.根据权利要求1所述的聚硅烟气防腐涂料的制备方法，其特征在于，在将聚硅烷改性环氧树脂、钛白粉及云母粉...
【专利技术属性】
技术研发人员：刘键，
申请(专利权)人：砺剑防务技术集团有限公司，
类型：发明
国别省市：广东,44