The invention discloses a preparation method of two-dimensional nanosheets. The preparation method is that ammonia water is added into the mixed solution of manganese acetate and nickel acetate to stir the reaction, and then the precipitates obtained are successively subjected to high temperature reaction, centrifugal separation, washing and drying to prepare Mn0.11Ni0.89 (OH) 2 two-dimensional nanosheets. The reaction temperature is 110 130 C. The invention adopts the hydrothermal method, and the preparation conditions are mild, and the process is simple and energy saving. The Mn0.11Ni0.89 (OH) 2 nanosheets have great potential applications in capacitors, batteries and electrocatalysis.
【技术实现步骤摘要】
一种二维纳米片的制备方法
本专利技术属于新材料
，具体涉及一种二维纳米片的制备方法。
技术介绍
氢氧化镍具有独特的层状结构、优异的电化学性能、低成本和无污染的特性，在超级电容器和水的电催化氧化领域是一种很有竞争力的电极材料。但是，作为超级电容器的电极材料，氢氧化镍的比电容远低于理论值，且循环稳定性差。材料的性能取决于材料本身的大小、形貌和晶体结构。所以，材料科学的热点是控制材料的形貌和结构。在晶体生长过程中，形貌的演变主要取决于生长环境。外来物质在生长环境中起到了重要的作用。在合成系统中加入添加剂来诱导生成新的晶体形貌是一个有效的方法。因为添加剂可能影响原子构型，从而改变表面稳定性。多缺陷的晶体有利于提高法拉第电容器的比电容。二维纳米片状结构的氢氧化镍能够提供较大的层间间距，有利于离子的快速交换，同时也增大了电化学活性材料和电解液之间的接触面积。用其它金属离子取代镍离子能够产生多相的金属氢(氧)化物并诱导丰富的结构缺陷。从理论上讲，电极反应时，在晶格间引入非活性的金属离子能够稳定α-Ni(OH)2的晶体结构。从而能够显著地提高α-Ni(OH)2电极的比电容和...
【技术保护点】
1.一种二维纳米片的制备方法，其特征在于，所述制备方法是先在乙酸锰与乙酸镍的混合溶液中加入氨水搅拌反应，之后将得到的沉淀物依次经高温反应、离心分离、洗涤和干燥后，制得Mn0.11Ni0.89(OH)2二维纳米片；所述高温反应的反应温度为110‑130℃。
【技术特征摘要】
1.一种二维纳米片的制备方法，其特征在于，所述制备方法是先在乙酸锰与乙酸镍的混合溶液中加入氨水搅拌反应，之后将得到的沉淀物依次经高温反应、离心分离、洗涤和干燥后，制得Mn0.11Ni0.89(OH)2二维纳米片；所述高温反应的反应温度为110-130℃。2.根据权利要求1所述二维纳米片的制备方法，其特征在于，所述乙酸锰与乙酸镍的摩尔比为1:1-8。3.根据权利要求1所述二维纳米片的制备方法，其特征在于，所述乙酸锰与乙酸镍的混合溶液中溶剂水的体积和氨水的体积比为15-25:1。4.根据权利要求1所述二维纳米片的制备方法，其特征在于，所述乙酸锰与乙酸镍的混合溶液是将乙酸锰与乙酸镍溶解于蒸馏水中，且搅拌均匀后得到；所述加入氨水搅拌反应是采用边搅拌边加入氨水的方式将氨水加入混匀后的混合...
【专利技术属性】
技术研发人员：刘荣梅，江紫翔，汪越哲，舒畅，孙雪莹，
申请(专利权)人：安徽工程大学，
类型：发明
国别省市：安徽,34