A transfer coating anticorrosion method for polymer power lithium-ion battery material comprises the following steps: 1) feeding: controlling the tension of raw material coil to be 20-60 kg; 2) coating: controlling the tension of material coil to be 50-100 kg; 3) drying: controlling the tension of material coil to be 50-100 kg; 4) feeding: controlling the tension of material coil to be 50-100 kg; The tension is 50 ~ 100kg. The invention controls tension strictly and finely, and then spreads uniformly on the surface of the material directly by transfer coating method. It can be accomplished by using only ordinary transfer coating equipment, which not only saves more than 50% of the cost, but also increases the production speed several times or even dozens of times.
【技术实现步骤摘要】
一种聚合物动力锂离子电池材料的转移涂覆式防腐方法
本专利技术属于合物动力锂离子电池的制备
，具体涉及一种聚合物动力锂离子电池材料的转移涂覆式防腐方法。
技术介绍
聚合物锂离子电池在新能源EV电池应用中，以其重量轻，能量密度高，安全性优越等性能越来越受到个厂商的重视，聚合物锂离子电池的外包装材料的耐腐蚀表面处理就显的非常重要。行业中目前采用药液水浴式或喷淋式对聚合物锂离子电池表面存在一下问题：1、金属材料两面都进行了处理，电池应用中只需要内层(接触电解液的那一层)做处理即可，无需两面都处理，增加了设备的投入成本。2、药液水浴式或喷淋式处理需要使用水来进行表面清洗，浪费水资源且排放会造成水的污染。3、处理药液材料多消耗一倍。4、处理速度慢只有2米/分钟的速度5、无法进行局部处理6、对场地有严格要求，需要具有资质的化工园区才能生产。
技术实现思路
为解决现有技术存在的聚合物锂离子电池表面防腐处理存在严重浪费的缺陷，本专利技术提供一种聚合物动力锂离子电池材料的转移涂覆式防腐方法。1、一种聚合物动力锂离子电池材料的转移涂覆式防腐方法，其特征在于，包括以下步骤：1)、放料：...
【技术保护点】
1.一种聚合物动力锂离子电池材料的转移涂覆式防腐方法，其特征在于，包括以下步骤：1)、放料：将卷式的原材料开卷放出，在出卷方向上设置张力检测辊，控制原材料卷的张力值为20～60kg；2)、涂布：将处理液均匀涂布到材料表面，控制材料卷的张力值为50～100kg；3)、烘干：将涂布到材料表面的水性溶剂蒸发烘干，控制材料卷的张力为50～100kg；4)、收料：在入料方向上设置张力检测辊，控制材料卷的张力为50～100kg。
【技术特征摘要】
1.一种聚合物动力锂离子电池材料的转移涂覆式防腐方法，其特征在于，包括以下步骤：1)、放料：将卷式的原材料开卷放出，在出卷方向上设置张力检测辊，控制原材料卷的张力值为20～60kg；2)、涂布：将处理液均匀涂布到材料表面，控制材料卷的张力值为50～100kg；3)、烘干：将涂布到材料表面的水性溶剂蒸发烘干，控制材料卷的张力为50～100kg；4)、收料：在入料方向上设置张力检测辊，控制材料卷的张力为...
【专利技术属性】
技术研发人员：李学兵，黄桂东，汪如娟，周佃国，季莹莹，王莹，高正林，滕布军，
申请(专利权)人：连云港海创电子科技有限公司，
类型：发明
国别省市：江苏,32