本发明专利技术提供废气净化用催化剂以及使用此催化剂的废气净化方法，涉及废气净化技术领域，包括堇青石蜂窝陶瓷载体，所述堇青石蜂窝陶瓷载体内涂覆有高比表面积的γ‑Al2O3层，所述γ‑Al2O3内添加有镧和锶，所述γ‑Al2O3层上附着有活性催化成分，所述活性催化成分由镍、铑、钯、稀土氧化物、二氧化铈组成，具有贵金属用量少，成本低，热稳定性好的优点。

Catalyst for exhaust gas purification and exhaust gas purification method using the catalyst

The invention provides a catalyst for waste gas purification and a waste gas purification method using the catalyst, and relates to the technical field of waste gas purification, including a cordierite honeycomb ceramic carrier coated with a high specific surface area of a gamma_Al2O3 layer, the gamma_Al2O3 layer added with lanthanum and strontium, and the gamma_Al2O3 layer on the cordierite honeycomb ceramic carrier. The active catalytic component is composed of nickel, rhodium, palladium, rare earth oxides and cerium dioxide. It has the advantages of low consumption of precious metals, low cost and good thermal stability.

【技术实现步骤摘要】
废气净化用催化剂以及使用此催化剂的废气净化方法
本专利技术涉及废气净化
，具体涉及废气净化用催化剂以及使用此催化剂的废气净化方法。
技术介绍
汽车是现代社会最普及的交通工具，特别是近些年来私家车越来越多，所排放的废气所造成的的环境问题不容忽视，在我国汽车尾气净化是解决汽车尾气排放污染的最有效方法，通过催化剂可以净化这些有害废气。目前，使用的是使用贵金属如Pt、Pd作为废气控制催化剂，其具有高的活性，是优良的废气净化催化剂，但是其价格昂贵，资源少，而且热稳定性也有待提高，因此，如何降低贵金属的用量和提高催化剂的热稳定性一直是目前废气净化用催化剂的研究热点。
技术实现思路
(一)解决的技术问题针对现有技术的不足，本专利技术提供了一种废气净化用催化剂以及使用此催化剂的废气净化方法，具有贵金属用量少，成本低，热稳定性好的优点。(二)技术方案为实现以上目的，本专利技术通过以下技术方案予以实现：废气净化用催化剂，包括堇青石蜂窝陶瓷载体，所述堇青石蜂窝陶瓷载体内涂覆有高比表面积的γ-Al2O3层，所述γ-Al2O3内添加有镧和锶，所述γ-Al2O3层上附着有活性催化成分，所述活性催化成分由镍、铑本文档来自技高网...

【技术保护点】
1.废气净化用催化剂，其特征在于，包括堇青石蜂窝陶瓷载体，所述堇青石蜂窝陶瓷载体内涂覆有高比表面积的γ‑Al2O3层，所述γ‑Al2O3内添加有镧和锶，所述γ‑Al2O3层上附着有活性催化成分，所述活性催化成分由镍、铑、钯、稀土氧化物、二氧化铈组成。

【技术特征摘要】
1.废气净化用催化剂，其特征在于，包括堇青石蜂窝陶瓷载体，所述堇青石蜂窝陶瓷载体内涂覆有高比表面积的γ-Al2O3层，所述γ-Al2O3内添加有镧和锶，所述γ-Al2O3层上附着有活性催化成分，所述活性催化成分由镍、铑、钯、稀土氧化物、二氧化铈组成。2.如权利要求1所述的废气净化用催化剂，其特征在于，所述镧和锶的质量比为1.2-1.5:1。3.如权利要求1所述的废气净化用催化剂，其特征在于，所述镧和锶的总质量为γ-Al2O3质量的2.5-5％。4.如权利要求1所述的废气净化用催化剂，其特征在于，所述活性催化成分中含量由大到小顺序为镍、铑、钯。5.如权利要求1所述的废气...

【专利技术属性】
技术研发人员：钟华，
申请(专利权)人：安徽国能亿盛环保科技有限公司，
类型：发明
国别省市：安徽,34