The invention discloses a cement clinker and a preparation method thereof, comprising the following weight percentage raw materials: limestone 60-80%, pulverized coal 5-15%, clay 5-15%, iron powder 1-2%, arsenic-containing waste slag and/or non-ferrous metal smelting tailings 1-28%. The cement clinker described in the invention takes arsenic-bearing waste slag and tailings slag as one of raw materials of cement raw materials, mixes part of metal smelting tailings slag, and uses high temperature sintering under oxygen-enriched condition to produce cement clinker. The method does not increase additional energy consumption, but also provides raw materials and heat energy for cement clinker production, saves coal combustion and produces simultaneously. The emission of natural smoke and smoke can reach the national standard.
【技术实现步骤摘要】
一种水泥熟料及其制备方法
本专利技术属于水泥熟料制备
，具体涉及一种水泥熟料及其制备方法。
技术介绍
水泥易烧性能是影响水泥烧成的一个重要参数，同时也是影响水泥质量的一个重要因素。生料易烧性，理论上指生料组分是否容易转变成水泥熟料相物质，而实际评价通常用生料按一定制度煅烧后，测定熟料中f-Cao的含量来衡量。水泥熟料中游离氧化钙低于1.0%时，一般认为熟料已经烧成。通常认为，尾矿及废渣中的硅、钙、铝、铁等氧化物，还有丰富的微量元素均可以作为水泥原料使用，并且这些微量元素对增加水泥熟料液相，改善液相性质有益。当然，其中的磷、硼、锆、磷、等不利元素也会影响水泥性能，微量元素和氧化物的过量添加也会对水泥熟料的凝结时间、安定性、强度等有影响，特别是有毒的砷等元素不能稳定固化在水泥中会对人体有危害，游离的砷元素也会降低水泥的强度。我国的砷矿资源丰富，探明储量为世界总储量的70％。但由于自然界的砷，绝大多数是与各种有色金属矿物共生，除砷精矿以外，几乎所有的精矿都对As的含量提出了控制要求，精矿中砷的存在，不但降低了精矿的品质，而且对后续的冶炼过程造成严重影响，因此通常将...
【技术保护点】
1.一种水泥熟料，其特征在于包括以下重量百分比的原料：石灰石60～80%、煤粉5～15%、粘土5～15%、铁粉1～2%、含砷废渣和/或有色金属冶炼尾渣1～28%。
【技术特征摘要】
1.一种水泥熟料，其特征在于包括以下重量百分比的原料：石灰石60～80%、煤粉5～15%、粘土5～15%、铁粉1～2%、含砷废渣和/或有色金属冶炼尾渣1～28%。2.根据权利要求1所述的水泥熟料，其特征在于所述的各种原材料中的水分含量均低于1%。3.根据权利要求1所述的水泥熟料，其特征在于所述的粘土由煤矸石、页岩中任意一种或几种代替，所述的铁粉由铁矿石、赤泥、锡冶炼渣中任意一种或几种代替。4.根据权利要求1所述的水泥熟料，其特征在于所述的含砷废渣是指硫铁矿制酸得到的硫酸烧渣、含砷废水、废酸沉渣、含砷烟气沉降得到的灰渣中的一种或任意几种的混合物，所述的含砷废渣的含砷量为0.1～20%。5.根据权利要求1所述的水泥熟料，其特征在于所述的有色金属冶炼尾矿渣包括铅锌尾矿、磁铁矿尾矿、电解金属锰渣、冶炼铜渣中的一种或任意几种的混合物。6.根据权利要求1所述的水泥熟料，其特征在于所...
【专利技术属性】
技术研发人员：于站良，饶永福，郭鲜艳，
申请(专利权)人：云南创拓环境科技有限公司，
类型：发明
国别省市：云南,53
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。