The invention relates to a preparation method of sea urchin-like vanadium oxide nanometer material, belonging to the field of nanometer material preparation. The invention preoxidizes two-dimensional vanadium carbide V2C by microwave and then proceeds to secondary oxidation in air (oxygen), thereby preparing sea urchin-like vanadium oxide nanomaterials. In addition to the sea urchin-like morphology and the preservation of the original V2C lamellar structure, the product has a good application prospect in lithium-ion batteries and supercapacitors. The novel sea urchin-like vanadium oxide nanomaterials prepared by this method have excellent morphology, high specific surface area, high battery capacity and good cycling performance. In addition, the method is simple, inexpensive, and controllable in preparation conditions. The sea urchin like vanadium oxide nanomaterials are mainly used for electrode materials.
【技术实现步骤摘要】
一种海胆状钒氧化物纳米材料的制备方法
本专利技术涉及一种海胆状钒氧化物纳米材料的制备方法，属于纳米材料制备的
技术介绍
近年来，钒氧化物因高比容量以及丰富的资源，已经广泛应用到电极材料。相比传统方法制备的钒氧化物，纳米形态的钒氧化物以其独特的形貌和优异的电化学性能，受到了越来越多的关注。近年来，一类新型二维晶体材料MXenes受到材料研究者的广泛关注(Naguib,M.,etal.,AdvancedMaterials,2014.26(7):992-1005)。MXenes(化学式Mn+1Xn，n＝1、2、3，M为早期过渡族金属，X为碳和/或氮)具有与石墨烯类似的二维层状结构，且具有较大的比表面积和较窄的带隙宽度，常温环境性质稳定，但在一定条件下如高温或水溶液中易被氧化。二维碳化钒(V2C)作为一种典型的MXenes材料，具有类石墨烯层状结构。研究发现，二维碳化钒(V2C)氧化后会形成对应的纳米钒氧化物。因此，选择合适的氧化工艺，将V2C氧化，可控制氧化产物的形貌和性能。
技术实现思路
技术问题：本专利技术的目的在于：针对上述观点，提供一种海胆状钒氧化物纳米材...
【技术保护点】
1.一种海胆状钒氧化物纳米材料的制备方法，其特征在于，该制备方法将二维碳化钒加入水后进行微波加热预氧化，再空气气氛加热二次氧化，得到海胆状钒氧化物纳米材料。
【技术特征摘要】
1.一种海胆状钒氧化物纳米材料的制备方法，其特征在于，该制备方法将二维碳化钒加入水后进行微波加热预氧化，再空气气氛加热二次氧化，得到海胆状钒氧化物纳米材料。2.根据权利要求1所述的海胆状钒氧化物纳米材料的制备方法，其特征在于：所述的微波加热预氧化过程的微波加热，加热功率为700～1800瓦。3.根据权利要求1所述的海胆状钒氧化物纳米材料的制备方法，其特征在于：所述的微波加热预氧化过程的微波加热，在微波炉中氧化，取出冷却后重复微波氧化多次，累计氧化处理时间为1～10分钟，温度为200～1000℃。4...
【专利技术属性】
技术研发人员：孙正明，王英，郑伟，张培根，田无边，张亚梅，
申请(专利权)人：东南大学，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。