The invention discloses a H13 steel-based self-lubricating hot working die material, which comprises a matrix, a lubricating phase and a hard phase. The matrix is a H13 steel powder, the lubricating phase is a mixture of CaF2 and MoS2, and the hard phase is Cr2C3. The matrix, a lubricating phase and a hard phase three-phase powder are evenly mixed by a ball mill, and then are powder metallurgical. Methods the hot working die material was prepared. The hot working die made of H13 steel-based self-lubricating material can realize self-lubricating work without additional lubricant, reduce friction and wear between the die and the workpiece, and realize cleaner production.
【技术实现步骤摘要】
H13钢基自润滑热作模具材料及制备方法
本专利技术涉及热作模具
，尤其涉及一种H13钢基自润滑热作模具材料及制备方法。
技术介绍
随着现代工业技术的发展，许多高端装备摩擦副工作在高温、高压等极端工况条件下。高温下工作的零部件的摩擦、磨损及润滑问题，显得格外突出。热作模具工作时摩擦条件异常严酷，模具温度极高，工作部分热磨损十分严重，导致模具寿命低。润滑油一般工作温度低于180℃，润滑脂的工作温度为80-100℃，高温润滑脂工作温度一般低于300℃，这些都不能满足工况温度大于300℃以上的情况，造成润滑剂利用率极低，润滑效果差，同时污染生产环境，影响生产人员的健康，从而影响现代产业工人的职业导向。研究环保无污染的新型润滑方式，可促进零部件成形产业的可持续发展。高温自润滑材料本身具有减摩、抗磨和润滑功能，可在无外加润滑剂的条件下实现自润滑工作。研究能够满足热作模具服役环境所要求的高温机械强度与尺寸稳定性的高温自润滑材料，是在工业上解决该问题的途径之一。将自润滑材料应用在热作模具上，可减小模具与工件的摩擦与磨损，省去润滑系统，避免切削液造成的环境污染，可实现清洁化生...
【技术保护点】
1.一种H13钢基自润滑热作模具材料，其特征在于，包括基体、润滑相以及硬质相，其中，基体为H13钢粉末，润滑相为CaF2和MoS2的混合物，硬质相为Cr2C3，利用球磨机将基体、润滑相以及硬质相三相粉末混合均匀，再通过粉末冶金的方法制备得到热作模具。
【技术特征摘要】
1.一种H13钢基自润滑热作模具材料，其特征在于，包括基体、润滑相以及硬质相，其中，基体为H13钢粉末，润滑相为CaF2和MoS2的混合物，硬质相为Cr2C3，利用球磨机将基体、润滑相以及硬质相三相粉末混合均匀，再通过粉末冶金的方法制备得到热作模具。2.如权利要求1所述的H13钢基自润滑热作模具，其特征在于，H13钢粉末的质量分数为：65%~85%，Cr2C3的质量分数为：10%~20%，CaF2的质量分数为：2.5%~10%，MoS2：2.5%~5%。3.如权利要求1所述的H13钢基自润滑热作模具材料，其特征在于，基体：选取粒度-200~+500目的H13钢粉末；润滑相：选取-200~+300目的CaF2粉末、MoS2粉末；硬质相：选取-200~+500目的Cr2C3粉末。4.一种基于权利要求1至3中任意一项所述的H13钢基自润滑热作模具材料的制...
【专利技术属性】
技术研发人员：王华君，李梦璐，姚振华，燕松山，曾鲜，周春杨，杨浩，
申请(专利权)人：武汉理工大学，
类型：发明
国别省市：湖北,42
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。