少变形木塑发泡层配方组成比例

本发明专利技术公开了一种少变形木塑发泡层配方，质量份组成为：聚氯乙烯(PVC)树脂100份、木粉26份、氯化聚乙烯(CPE)9份、SiC纳米粉末5份、纳米活性碳酸钙5份、钙锌复合稳定剂5份、聚酯增塑剂10份、硼酸酯偶联剂1.4份、AC发泡剂1.5份、碳酸氢钠0.7份、发泡调节剂6份、硬脂酸甘油脂0.5份、硅酮加工助剂3份。本发明专利技术耐磨性、强度高，且不易变形、开裂。

Formulation of less deformation wood plastic foam layer

The invention discloses a formulation of a low deformation wood-plastic foaming layer, which consists of 100 parts of PVC resin, 26 parts of wood flour, 9 parts of CPE, 5 parts of SiC nano-powder, 5 parts of nano-active calcium carbonate, 5 parts of calcium-zinc composite stabilizer, 10 parts of polyester plasticizer, 1.4 parts of borate coupling agent, 1.5 parts of AC foaming agent, etc. 0.7 sodium bicarbonate, 6 foaming regulators, 0.5 stearic glycerides and 3 processing auxiliaries. The invention has high abrasion resistance and high strength, and is not easy to deform and crack.

【技术实现步骤摘要】
少变形木塑发泡层配方
本专利技术涉及一种高分子复合材料配方，特别是一种木塑发泡层配方。
技术介绍
木塑复合板材设有木塑发泡层，木塑发泡层是通过发泡而成，容易变形，耐磨性也较差。
技术实现思路
本专利技术针对现有技术的不足，提出一种能显著减少变形，并能显著提高耐磨性的少变形木塑发泡层配方。本专利技术通过下述技术方案实现技术目标。少变形木塑发泡层配方，其改进之处在于：质量份组成为：聚氯乙烯(PVC)树脂100份、木粉26份、氯化聚乙烯(CPE)9份、SiC纳米粉末5份、纳米活性碳酸钙5份、钙锌复合稳定剂5份、聚酯增塑剂10份、硼酸酯偶联剂1.4份、AC发泡剂1.5份、碳酸氢钠0.7份、发泡调节剂6份、硬脂酸甘油脂0.5份、硅酮加工助剂3份。本专利技术与现有技术相比，具有以下积极效果：1、SiC纳米粉末，大大增强了本专利技术耐磨性和强度，且不易变形、开裂。2、加入硅酮加工助剂，有利于增加物料的流动性，易于冲模成形，有利于提高本专利技术的内在质量和表面光洁度。具体实施方式下面结合实施例对本专利技术作进一步说明。少变形木塑发泡层配方，质量份组成为：聚氯乙烯(PVC)树脂100份、木粉26份、氯化聚乙烯(CPE)9份、SiC纳米粉末5份、纳米活性碳酸钙5份、钙锌复合稳定剂5份、聚酯增塑剂10份、硼酸酯偶联剂1.4份、AC发泡剂1.5份、碳酸氢钠0.7份、发泡调节剂6份、硬脂酸甘油脂0.5份、硅酮加工助剂3份。

【技术保护点】
1.一种少变形木塑发泡层配方，其特征在于：质量份组成为：聚氯乙烯(PVC)树脂100份、木粉26份、氯化聚乙烯(CPE)9份、SiC纳米粉末5份、纳米活性碳酸钙5份、钙锌复合稳定剂5份、聚酯增塑剂10份、硼酸酯偶联剂1.4份、AC发泡剂1.5份、碳酸氢钠0.7份、发泡调节剂6份、硬脂酸甘油脂0.5份、硅酮加工助剂3份。

【技术特征摘要】
1.一种少变形木塑发泡层配方，其特征在于：质量份组成为：聚氯乙烯(PVC)树脂100份、木粉26份、氯化聚乙烯(CPE)9份、SiC纳米粉末5份、纳米活性碳酸钙...

【专利技术属性】
技术研发人员：郭新，
申请(专利权)人：郭新，
类型：发明
国别省市：江苏,32