A marine alkaline Silicon-manganese sintered flux and its preparation method are described. The composition of the flux is as follows: CaF2:50_65%, SiO2:30~40%, MnO:5_10%; the mass percentage of each component is 100%; the preparation method is as follows: 1) According to the composition proportion of marine alkaline Silicon-manganese sintered flux, the composition of the flux is weighed. After each raw material is mixed evenly, the dry-mixed raw material is prepared, and then the water glass and the dry-mixed raw material are mixed wetly to produce the wet-mixed material; 2) the wet-mixed material is granulated to obtain the semi-finished product and then dried at low temperature; 3) the semi-finished product is sintered to produce the high-alkaline Silicon-manganese type sintering flux for ships; the present invention uses the alkaline Silicon-manganese type sintering flux for ships, after welding. The properties of the welded joints are as follows: tensile strength is 650-700 MPa, impact energy at low temperature (40) is 54-69J.
【技术实现步骤摘要】
一种船用高碱度硅锰型烧结焊剂及其制备方法
本专利技术属于焊接
,具体是一种船用高碱度硅锰型烧结焊剂及其制备方法。
技术介绍
埋弧焊焊剂是埋弧焊主要的消耗材料之一,在焊接过程中对焊缝金属起机械保护、冶金处理及改善焊接工艺性能的作用,焊剂的焊接工艺性能和化学冶金性能是决定焊缝金属质量的重要因素。相比熔炼焊剂,烧结焊剂具有烧结焊剂具有能耗低、碱度调节范围大、易脱氧、易于合金化、易于生产等优点。高碱度氟碱型焊剂中酸性氧化物含量较少,焊剂氧化性弱,抗气孔能力强,有利于获得高低温韧性的焊缝金属。为满足工业化生产对性能优良的焊剂的紧迫需求,有必要制备一种性能优良、能够实现焊缝金属强度和高的低温韧性,同时具有光滑的焊道,良好脱渣性的高碱度氟碱型烧结焊剂。
技术实现思路
针对现有技术的不足,本专利技术提供了一种船用高碱度硅锰型烧结焊剂及其制备方法;本专利技术满足船板钢焊接工艺对性能优良的焊剂的紧迫需求,研制了一种焊接过程稳定、焊缝金属强度高,低温韧性高,焊缝成分和组织均匀、焊道表面光滑、脱渣性能良好的烧结焊剂。一种船用高碱度硅锰型烧结焊剂,其含有成分按质量百分比为:CaF2:50-65%,SiO2:30~40%,MnO:5-10%,各组分的质量百分比总和为100%。所述的船用高碱度硅锰型烧结焊剂,焊后所得的焊接接头性能指标如下:抗拉强度强度为650~700MPa,低温冲击功(-40℃)为54~69J。本专利技术的船用高碱度硅锰型烧结焊剂的制备方法,包括如下步骤:步骤1,混料:(1)按船用高碱度硅锰型烧结焊剂的成分配比,秤取各原料后,混合均匀,制得干混原料;(2)按质量比, ...
【技术保护点】
1.一种船用高碱度硅锰型烧结焊剂,其特征在于,其含有成分按质量百分比为CaF2:50‑65%,SiO2:30~40%,MnO:5‑10%;其中,按质量比,各组分的质量百分比总和为100%。
【技术特征摘要】
1.一种船用高碱度硅锰型烧结焊剂,其特征在于,其含有成分按质量百分比为CaF2:50-65%,SiO2:30~40%,MnO:5-10%;其中,按质量比,各组分的质量百分比总和为100%。2.根据权利要求1所述的一种船用高碱度硅锰型烧结焊剂,其特征在于,所述船用高碱度硅锰型烧结焊剂,焊后所得的焊接接头性能指标如下:抗拉强度强度为650~700MPa,低温冲击功(-40℃)为54~69J。3.权利要求1所述的船用高碱度硅锰型烧结焊剂的制备方法,其特征在于,包括如下步骤:步骤1,混料:(1)按船用高碱度硅锰型烧结焊剂的成分配比,秤取各原料后,混合均匀,制得干混原料;(2)按质量比,水玻璃:干混原料=20~30%,将水玻璃和干混原料进行湿混,制得湿混料;步骤2,造粒:(1)将湿混料进行一...