The invention provides a preparation method of ketimide curing agent, which comprises the following operations: mixing amine compounds with ketones, heating reflux reaction, and removing water generated in the reaction to obtain ketimide curing agent; the amine compound is one of low molecular polyamide, cashew phenol modified amine and phenolic amine; the ketone is a methyl Ethyl ketone or methyl isobutyl ketone. The invention also provides a ketone imide curing agent obtained from the preparation method and its application. The new ketimide curing agent synthesized by this method has the advantages of excellent curing properties, non-toxicity and health, being suitable for wet surface or environment and being latent.
【技术实现步骤摘要】
一种酮亚胺固化剂的制备及应用
本专利技术属于涂料领域，具体涉及环氧树脂的固化剂的制备方法及应用。
技术介绍
环氧树脂所用的酮亚胺固化剂是用酮和有机伯胺经反应脱水后形成的，该固化剂具有一定的潜伏性，在有水的环境下使用时，水与酮亚胺固化剂反应形成胺和酮(酮亚胺合成反应的逆反应)，该胺与环氧树脂反应可实现环氧树脂的交联固化。现有的酮亚胺是用酮(甲基乙基酮、甲基异丁基酮等)和乙二胺、二乙烯三胺、间苯二胺等小分子胺合成的，该类酮亚胺在与环氧树脂的固化应用时，由于吸水后释放出的乙二胺、二乙烯三胺和间苯二胺等具有低沸点和毒性大的特点，因此造成了施工过程中人员易过敏甚至中毒和固化的环氧树脂易脆和表面容易形成胺霜等质量问题。胺霜是涂层内小分子胺释放出来，在涂层表面形成的碳酸铵、碳酸盐等物质，对涂层造成了破坏。
技术实现思路
针对现有技术中传统酮亚胺固化剂的毒性大、涂层强度低缺点，本专利技术的目的是提出一种酮亚胺固化剂的制备方法。本专利技术的第二个目的是提出所述制备方法得到的固化剂。本专利技术的第三个目的是提出所述固化剂的应用。实现本专利技术上述目的的技术方案为：一种酮亚胺固化剂的制备方...
【技术保护点】
1.一种酮亚胺固化剂的制备方法，其特征在于，包括以下操作：把胺类化合物和酮混合，加热回流反应，并除去反应过程中产生的水，得到酮亚胺固化剂；所述胺类化合物为低分子聚酰胺、腰果酚改性胺、酚醛胺中的一种；所述酮为甲基乙基酮或甲基异丁基酮。
【技术特征摘要】
1.一种酮亚胺固化剂的制备方法，其特征在于，包括以下操作：把胺类化合物和酮混合，加热回流反应，并除去反应过程中产生的水，得到酮亚胺固化剂；所述胺类化合物为低分子聚酰胺、腰果酚改性胺、酚醛胺中的一种；所述酮为甲基乙基酮或甲基异丁基酮。2.根据权利要求1所述酮亚胺固化剂的制备方法，其特征在于，所述低分子聚酰胺的胺值为150-600mgKOH/g。3.根据权利要求1所述酮亚胺固化剂的制备方法，其特征在于，胺类化合物和酮的质量比为1∶(1-2)。4.根据权利要求1所述酮亚胺固化剂的制备方法，其特征在于，回流反应使用的反应容器上装有分水器，用分水器除去反应中产生的水；反应后蒸发除去挥发性物质。5.根据权利要求1-4任一项所述酮亚胺固化剂的制备方法，其特征在于，反应时间为2-4小时。6.权利要求1-5任一项所述的制备方法得到的酮亚胺固化剂。...
【专利技术属性】
技术研发人员：张建红，
申请(专利权)人：西安天元化工有限责任公司，
类型：发明
国别省市：陕西,61