The invention relates to a modified polyamide 46, which is composed of 100 parts of polyamide 46 resin, 0-20 parts of toughening agent, 20-50 parts of bromine flame retardant, 0.5-2 parts of antioxidant, 0.5-2 parts of heat stabilizer and glass fiber. The dosage of the glass fiber is 20% to 40% of the total weight of each component. The invention also relates to the preparation method of the modified polyamide 46 and its application in welding equipment. Compared with the existing technology, the modified polyamide 46 of the invention has high rigidity, high toughness and high temperature resistance, and its thermal deformation temperature can reach 290 C. It can be used as heat-resistant engineering plastics in the field of automatic welding of electronic and electrical appliances.
【技术实现步骤摘要】
一种改性聚酰胺46，其制备方法及其应用
本专利技术涉及阻燃高分子复合材料领域，具体涉及一种改性聚酰胺46，该改性聚酰胺46的制备方法，以及该改性聚酰胺46的应用。
技术介绍
聚酰胺46(全名为聚己二酰丁二胺，简称PA46)是一种具有高熔点和高结晶度的聚酰胺树脂，广泛应用于汽车配件和电子电器等应用领域。聚酰胺46与聚酰胺6和聚酰胺66相比较，分子链结构对称性高，酰胺基密度高，分子链有较好的规整性。在世界上，荷兰帝斯曼工程塑料公司(DSM)最早成功地确立了工业生产聚酰胺46的方法。但是，纯的聚酰胺46存在阻燃不好、缺口冲击低、热变形温度低等缺点，需要通过改性技术，使改性后的聚酰胺46达到高刚、高韧、耐高温的标准，能够作为高温工程塑料用于焊接设备中。鉴于此，特提出本专利技术。
技术实现思路
本专利技术的第一目的在于提供一种改性聚酰胺46。本专利技术的第二目的在于提供上述改性聚酰胺46的制备方法。本专利技术的第三目的在于提供上述改性聚酰胺46的应用。为实现上述目的，本专利技术的技术方案如下：本专利技术涉及一种改性聚酰胺46，其由包括以下重量份的组分制成：聚酰胺46树脂100份...
【技术保护点】
1.一种改性聚酰胺46，其特征在于，其由包括以下重量份的组分制成：聚酰胺46树脂100份，增韧剂0～20份，溴系阻燃剂20～50份，抗氧剂0.5～2份，热稳定剂0.5～2份，以及玻璃纤维，所述玻璃纤维的用量为上述各组分总重量的20％～40％。
【技术特征摘要】
1.一种改性聚酰胺46，其特征在于，其由包括以下重量份的组分制成：聚酰胺46树脂100份，增韧剂0～20份，溴系阻燃剂20～50份，抗氧剂0.5～2份，热稳定剂0.5～2份，以及玻璃纤维，所述玻璃纤维的用量为上述各组分总重量的20％～40％。2.根据权利要求1所述的改性聚酰胺46，其特征在于，其由包括以下重量份的组分制成：聚酰胺46树脂100份，增韧剂5～10份，溴系阻燃剂29～45份，抗氧剂0.5～2份，热稳定剂0.5～2份，以及玻璃纤维，所述玻璃纤维的用量为上述各组分总重量的30％～35％。3.根据权利要求1所述的改性聚酰胺46，其特征在于，所述增韧剂为聚酰胺聚合物，优选尼龙6。4.根据权利要求1所述的改性聚酰胺46，其特征在于，所述溴系阻燃剂中含有聚溴化苯乙烯和三氧化二锑，优选两者的质量比为(2～5)：1。5.根据权利要求1所述的改性聚酰胺46，其特征在于，所述抗氧剂选自N,N'-双-(3-(3,5-二叔丁基-4-羟基苯基)丙酰基)己二胺、三[2.4-二叔丁基苯基]亚磷酸酯、四[β-(3,5-二...
【专利技术属性】
技术研发人员：杨平，陈基武，徐江，
申请(专利权)人：深圳市优化新材料科技有限公司，
类型：发明
国别省市：广东,44