The invention discloses a high-performance conductive plastic, which comprises 55-65 parts of PVC, 15-20 parts of melamine resin, 10-15 parts of superconducting carbon black, 10-15 parts of zinc oxide powder, 6-8 parts of nanometer zirconia, 1-5 parts of glass fiber, 15-25 parts of titanium magnesium alloy powder and 1-5 parts of barium stearate. The invention belongs to the technical field of plastic materials. The high-performance conductive plastic proposed by the invention has the advantages of light weight, easy molding and high conductivity, and can be conveniently passed through molecular design. Synthetic or compounded materials of various structures are of low cost. It is suitable for electronic components, communication devices and other fields. It can resist electromagnetic interference and antistatic.
【技术实现步骤摘要】
一种高性能导电塑料
本专利技术属于塑料材料
,具体是指一种高性能导电塑料。
技术介绍
导电塑料是由树脂和导电物质混合而成,用塑料的加工方式进行加工的功能型高分子材料,大量应用于电子和电器领域、防爆产品的外壳及结构件、电缆中使用的半导电屏蔽料及电子产品的屏蔽外壳。目前,研制的导电塑料其成本相对较高,限制了其广泛应用。因此怎样制造出一种导电率高且制造成本低的高性能导电塑料是本领域技术人员亟待解决的问题。
技术实现思路
为解决上述现有难题,本专利技术提供了导电率高且制造成本低的高性能导电塑料。本专利技术采用的技术方案如下:一种高性能导电塑料,包括如下重量份的原料:聚氯乙烯55~65份、密胺树脂15~20份、超导电炭黑10~15份、氧化锌粉10~15份、纳米二氧化锆6~8份、玻璃纤维1~5份、钛镁合金粉15~25份、硬脂酸钡1~5份。进一步地,一种高性能导电塑料,包括如下重量份的原料:聚氯乙烯60份、密胺树脂16份、超导电炭黑12份、氧化锌粉12份、纳米二氧化锆7份、玻璃纤维3份、钛镁合金粉30份、硬脂酸钡4份。采用上述方案本专利技术取得有益效果如下:本专利技术所提出的高性能导电塑料,各组分协同作用,使塑料实现了从绝缘体到半导体再到导体的巨大转变,与传统材料相比,具有重量轻、易成型、导电率高的特点,并可以方便地通过分子设计合成或复合成多种结构的材料,成本低。适用于电子元器件、通讯器件等领域,可抗电磁波干扰和抗静电。具体实施方式下面将对本专利技术实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅是本专利技术的一部分实施例,而不是全部的实施例。基于本专利 ...
【技术保护点】
1.一种高性能导电塑料,其特征在于,包括如下重量份的原料:聚氯乙烯55~65份、密胺树脂15~20份、超导电炭黑10~15份、氧化锌粉10~15份、纳米二氧化锆6~8份、玻璃纤维1~5份、钛镁合金粉15~25份、硬脂酸钡1~5份。
【技术特征摘要】
1.一种高性能导电塑料,其特征在于,包括如下重量份的原料:聚氯乙烯55~65份、密胺树脂15~20份、超导电炭黑10~15份、氧化锌粉10~15份、纳米二氧化锆6~8份、玻璃纤维1~5份、钛镁合金粉15~25份、硬脂酸...