一种新型含Re屈氏体热处理用无铅镁浴合金制造技术

本发明专利技术公开了一种新型含Re屈氏体热处理用无铅镁浴合金及其加工工艺。按照重量百分比，该合金的成分为：Ba:1.5‑2.0wt.%,Re:0.4‑0.6wt.%,Sn:10.0‑20.0wt.%,Sc：0.4‑0.8wt.%，Ce:0.3‑0.5wt.%,Al:2.0‑5.0wt.%,余量为镁。采用该镁浴合金来替代铅浴合金进行热处理,所得到的屈氏体钢丝拉拔后可获得良好的综合性能，给成品钢帘线提供了所需的力学指标，同时减少了钢帘线在生产过程中断丝现。

A new lead-free magnesium bath alloy containing Re for heat treatment of austenite

The present invention discloses a new lead-free magnesium bath alloy containing Re and its processing technology. According to the weight percentage, the composition of the alloy is: Ba:1.5 2.0wt.%, Re:0.4 0.6wt.%, Sn:10.0 20.0wt.%, Sc:0.4 0.8wt.%, Ce:0.3 0.5wt.%, Al:2.0 5.0wt.%, and the allowance for magnesium. The magnesium bath alloy is used to replace the lead bath alloy for heat treatment. The obtained steel wire can obtain good comprehensive properties, provide the required mechanical indexes for the finished steel cord, and reduce the interruption of the steel cord in the production process.

【技术实现步骤摘要】
一种新型含Re屈氏体热处理用无铅镁浴合金
本专利技术涉及合金
，具体地说，涉及一种镁浴合金。
技术介绍
我国钢帘线的产量和结构品种逐年增加，钢帘线生产企业也一直致力于生产工艺的优化，通过设备改善和工艺调整，不断降低产各工序的断丝率，提高生产效率和综合成材率。在生产实践中淬火方式的改变，给钢帘线生产的稳定和效率带来了较大的提升。淬火是中高碳钢丝生产中的关键工序。帘线钢丝的铅浴淬火原理是根据钢的等温转变C曲线，让过冷奥氏体在600右的铅液中进行等温转变，产生细珠光体组织索氏体。钢丝通过淬火得到索氏体组织，这样的组织具有较高的拉伸极限，钢丝拉拔后可获得良好的综合性能，给成品钢帘线提供了所需的力学指标，同时减少了钢帘线在生产过程中断丝现。铅液所具有的高热容、耐热冲击的特性易于实现钢丝的等温转变。铅属于重金属，其熔点为327度。当加热至400-500度时，即有大铅蒸汽逸出，在空气中迅速氧化凝集，以氧化铅的烟尘逸散。故在生产过程中不可避免地导致车间内环境的铅污染。长期在铅污染环境中作业的工人，可能发生铅中毒职业危害。水浴淬火是在水中加入能溶解的高分子聚合物添加剂后，大大提高了水的黏度，将水本文档来自技高网...

【技术保护点】
1.一种新型含Re屈氏体热处理用无铅镁浴合金；按照重量百分比，该合金的成分为：Ba: 1.5‑2.0wt.%,Re:0.4‑0.6wt.% ,Sn: 10.0‑20.0wt.%,Sc：0.4‑0.8wt.%，Ce:0.3‑0.5wt.%, Al:2.0‑5.0wt.%,余量为镁。

【技术特征摘要】
1.一种新型含Re屈氏体热处理用无铅镁浴合金；按照重量百分比，该合金的成分为：Ba:1.5-2.0wt.%,Re:0.4-0.6wt.%,Sn:10.0-20.0wt.%,Sc：0.4-0.8wt.%，Ce:0.3-0.5wt.%,Al:2.0-5.0wt.%,余量为镁。2.根据权利要求1所述一种新型含Re屈氏体热处理用无铅镁浴合金，其特征在于包括如下步骤：将如上配比的原料加入到大气保护的感应电炉内，并...

【专利技术属性】
技术研发人员：杨长江，
申请(专利权)人：广州宇智科技有限公司，
类型：发明
国别省市：广东,44