热处理铅浴用高导热耐高温氯化物盐覆盖剂制造技术

本发明专利技术公开了热处理铅浴用高导热耐高温氯化物盐覆盖剂及其加工工艺。按照重量百分比，该合金的成分为：KCl:15.0‑18.0wt.%,SrCl2:3.0‑5.0wt.%,CaCl2:4.0‑8.0wt.%,FeCl2：2.0‑5.0wt.%，B2O3:3.0‑8.0wt.%,ZnO:1.0‑2.0wt.%,余量为CaO。该覆盖剂的研制将解决铅浴热处理工艺应用中的难题，为铅浴热处理的推广起到至关重要的作用，对工业生产也将具有重大的经济意义。

High thermal conductivity and high temperature chloride salt covering agent for heat treatment lead bath

The invention discloses a high heat conduction and high temperature chloride salt covering agent for heat treatment lead bath and its processing technology. According to the weight percentage, the composition of the alloy is: KCl:15.0 18.0wt.%, SrCl2:3.0 5.0wt.%, CaCl2:4.0 8.0wt.%, FeCl2:2.0 5.0wt.%, B2O3:3.0 8.0wt.%, ZnO:1.0 2.0wt.%. The development of the covering agent will solve the problems in the application of the lead bath heat treatment process and play a vital role in the popularization of the lead bath heat treatment. It will also have great economic significance for the industrial production.

【技术实现步骤摘要】
热处理铅浴用高导热耐高温氯化物盐覆盖剂
本专利技术涉及合金
，具体地说，涉及一种铅合金覆盖剂。
技术介绍
我国钢帘线的产量和结构品种逐年增加，钢帘线生产企业也一直致力于生产工艺的优化，通过设备改善和工艺调整，不断降低生产各工序的断丝率，提高生产效率和综合成材率。在生产实践中淬火方式的改变，给钢帘线生产的稳定和效率带来了较大的提升。淬火是中高碳钢丝生产中的关键工序，尤其是最终热处理淬火工艺，钢丝通过淬火得到索氏体组织，这样的组织具有较高的拉伸极限，钢丝拉拔后可获得良好的综合性能，给成品钢帘线提供了所需的力学指标，同时减少了钢帘线在生产过程中断丝现象。帘线钢丝的淬火方式主要有铅浴淬火、砂床淬火、水浴淬火。铅浴淬火是将钢件奥氏体化后，进入熔铅中进行淬火冷却完成组织转变的过程，最终组织为细珠光体。这是在制造中碳钢及高碳钢的钢丝工艺中，为了获得适当组织以便容易拉拔及获得高质量的一种常用工艺。铅浴热处理是一种传统的钢丝热处理工艺，具有热容量大、导热率高、投资小、成本低、工艺易于控制，等温转变程度高、处理后钢丝性能好、质量稳定等优点。铅浴的缺点也是很明显的。（1）铅浴淬火虽已在许多企业得到广本文档来自技高网...

【技术保护点】
1.一种热处理铅浴用高导热耐高温氯化物盐覆盖剂；按照重量百分比，该合金的成分为：KCl: 15.0‑18.0wt.%,SrCl2:3.0‑5.0wt.%,CaCl2:4.0‑8.0wt.%,FeCl2：2.0‑5.0wt.%，B2O3:3.0‑8.0wt.%, ZnO:1.0‑2.0wt.%,余量为CaO。

【技术特征摘要】
1.一种热处理铅浴用高导热耐高温氯化物盐覆盖剂；按照重量百分比，该合金的成分为：KCl:15.0-18.0wt.%,SrCl2:3.0-5.0wt.%,CaCl2:4.0-8.0wt.%,FeCl2：2.0-5.0wt.%，B2O3:3.0-8.0wt.%,ZnO:1.0-2.0wt.%,余量为CaO。2.根据权利要求1所述热处理铅浴用高导热耐高温氯化物盐覆盖剂，其特征在于包括如下步骤：原料KCl，SrCl2，CaCl2，FeCl2，...

【专利技术属性】
技术研发人员：杨长江，
申请(专利权)人：广州宇智科技有限公司，
类型：发明
国别省市：广东,44