接近共晶成分含Fe-Co-Ni铅浴用覆盖铝合金制造技术

本发明专利技术公开了一种接近共晶成分的含Fe‑Co‑Ni铅浴用覆盖铝合金及其加工工艺。按照重量百分比，该合金的成分为：Ba:1.5‑2.0wt.%,Fe:2.0‑3.0wt.%,Co:1.5‑1.8wt.%,Ni：1.0‑2.0wt.%，Sb:1.0‑3.0wt.%,Th:0.2‑0.4wt.%,余量为铝。该覆盖合金降铅效果最好，使用期长，且不影响钢丝铅淬火的质量，便于工人操作，为钢丝铅浴炉淬火生产中的首选降铅方法。

Near eutectic composition containing Fe-Co-Ni lead bath for covering aluminum alloy

The invention discloses a covering aluminum alloy with Fe eutectic composition containing lead oxide bath containing Co, Ni and its processing technology. According to the weight percentage, the composition of the alloy is: Ba:1.5 2.0wt.%, Fe:2.0 3.0wt.%, Co:1.5 1.8wt.%, Ni:1.0 2.0wt.%, Sb:1.0 3.0wt.%, Th:0.2 0.4wt.%, and the residual amount of aluminum. The overlay alloy has the best effect on reducing lead, long period of use, and does not affect the quality of steel wire lead quenching. It is convenient for workers to operate, and it is the first lead reduction method in the quenching production of steel wire lead bath furnace.

【技术实现步骤摘要】
接近共晶成分含Fe-Co-Ni铅浴用覆盖铝合金
本专利技术涉及合金
，具体地说，涉及一种铝覆盖合金。
技术介绍
钢丝的热处理生产一般有等温冷却和连续冷却两种冷却方式，对于钢丝绳用半成品钢丝而言，一般选择等温冷却。钢丝中的奥氏体在临界温度以上是一种稳定相，一旦冷却到临界温度以下，则处于热力学的不稳定状态，称为过冷奥氏体。过冷奥氏体发生转变，形成新的稳定相。钢丝绳的制绳钢丝在生产过程中，要对冷轧盘条进行多次拉拔；为了消除半成品钢丝的加工硬化，保证钢丝获得良好的拉拔性能，就要对半成品钢丝进行热处理。金属线材制品行业生产钢丝绳用钢材基本都为中高碳钢，一般使用亚共析钢和过共析钢的线材，根据各自的过冷奥氏体等温转变动力学曲线。制绳钢丝的生产采用高温（500-650℃）转变，形成均匀的索氏体化组织，在实际生产过程中，通过控制转变温度和转变时间即可得到适合钢丝进一步拉拔的细小、均匀的索氏体组织。传统铅浴淬火工艺的原理是根据钢的等温转变C曲线，让过冷奥氏体在600℃左右的铅液中进行等温转变，产生适合深度拉拔的索氏体组织。由于铅在300℃以上开始融化，一直到900℃左右开始沸腾，有非常宽的液态状态本文档来自技高网...

【技术保护点】
1.一种接近共晶成分的含Fe‑Co‑Ni铅浴用覆盖铝合金；按照重量百分比，该合金的成分为：Ba: 1.5‑2.0wt.%,Fe:2.0‑3.0wt.% ,Co:1.5‑1.8wt.%,Ni：1.0‑2.0wt.%，Sb:1.0‑3.0wt.%, Th:0.2‑0.4wt.%,余量为铝。

【技术特征摘要】
1.一种接近共晶成分的含Fe-Co-Ni铅浴用覆盖铝合金；按照重量百分比，该合金的成分为：Ba:1.5-2.0wt.%,Fe:2.0-3.0wt.%,Co:1.5-1.8wt.%,Ni：1.0-2.0wt.%，Sb:1.0-3.0wt.%,Th:0.2-0.4wt.%,余量为铝。2.根据权利要求1所述一种接近共晶成分的含Fe-Co-Ni铅浴用覆盖铝合金，其特征在于包括如下步骤：将如上配比的原料加入到大气保护的感应电...

【专利技术属性】
技术研发人员：杨长江，
申请(专利权)人：广州宇智科技有限公司，
类型：发明
国别省市：广东,44