The utility model discloses a dehydrogenation disk used in the process of producing titanium powder by hydrogenating dehydrogenation process, which is mainly composed of a rectangular disk body. There are two intersecting stiffeners on the diagonal line inside the disc. A number of exhaust parts are provided in the titanium powder layer filled with the plate, the exhaust part is the bottom end seal and the top. The opening of the tube is provided with a number of vent holes on the side wall of the cylinder. The top of the exhaust part is higher than the height of the titanium hydride powder layer. The bottom of the exhaust part is inserted at the bottom of the titanium hydride layer. After repeated duplication, the distortion of the material is small and the height of the material is up to up to 8 10cm, and the dehydrogenation speed is fast. It has the advantages of short time, not easy to sinter and so on.
【技术实现步骤摘要】
一种氢化脱氢法生产钛粉过程中用的脱氢料盘
本技术属于钛粉生产
，特别涉及一种氢化脱氢法生产钛粉过程中用的脱氢料盘。
技术介绍
目前氢化脱氢方法(HDH)是生产钛粉最普遍的方法，氢化脱氢法生产钛粉的基本原理可用下式表示：氢化：Ti+x/2H2→TiHx(x＝1.88～1.99)t＞300℃脱氢：TiHx→Ti+x/2H2(x＝1.88～1.99)t＞300℃其工艺是先将原料进行氢化制得氢化钛粉，然后再将氢化钛粉在保护气氛下进行破碎分级，最后将破碎分级后的氢化钛粉在真空下进行脱氢处理，检验后得到合格钛粉，卧式脱氢炉采用的脱氢料盘大多为矩形不锈钢盘，这种料盘在多次重复使用后扭曲变形大，使用寿命短，盛装的料层高度一般只有4-6cm，生产效率低，若料层加厚，又容易导致脱氢时间长，产品发生烧结现象严重。
技术实现思路
为解决现有技术中存在的问题，本技术设计提供了一种氢化脱氢法生产钛粉过程中用的脱氢料盘，在多次重复使后，扭曲变形量小，盛装的料层高度可达到8-10cm，且脱氢速度快，时间短，产品不易烧结。本技术的技术方案如下所述：一种氢化脱氢法生产钛粉过程中用的脱氢料盘，主要由矩形...
【技术保护点】
1.一种氢化脱氢法生产钛粉过程中用的脱氢料盘，主要由矩形的盘体(1)构成，其特征在于盘体(1)内的对角线上设有两块相互交叉的加强筋板(2)，在盘体(1)内盛装的氢化钛粉(4)料层中设有若干排气部件(3)，排气部件(3)为底部端面密封、顶部开口的筒体，筒体的侧壁上设有若干排气孔，排气部件(3)的顶部开口高于氢化钛粉(4)料层高度，排气部件(3)的底部插入设置在氢化钛粉(4)料层底部。
【技术特征摘要】
1.一种氢化脱氢法生产钛粉过程中用的脱氢料盘，主要由矩形的盘体(1)构成，其特征在于盘体(1)内的对角线上设有两块相互交叉的加强筋板(2)，在盘体(1)内盛装的氢化钛粉(4)料层中设有若干排气部件(3)，排气部件(3)为底部端面密封、顶部开口的筒体，筒体的...
【专利技术属性】
技术研发人员：李勇，袁继维，徐展平，徐绍志，
申请(专利权)人：贵州省过程工业技术研究中心，贵州省钛材料研发中心有限公司，
类型：新型
国别省市：贵州,52