The invention provides a composite material for a robot shell and its preparation method. The following materials are prepared as follows: epoxy resin 30, 50 weight, 8 weight portion of salicylic acid benzyl ester, 5 weight portion of silicon carbide powder 1, 5 styrene 10 weight, three oxidation two antimony 2 6 weight portion, second TERT butyl 1 1 4 weight portion of peroxide Benzene, two methyl two octyl 6, 10 weight. Compared with the existing technology, the present invention is made of epoxy resin, salicylate, silicon carbide micro powder, styrene, three oxidation of antimony two, tert Ding Ji peroxide and phthalic two methyl two octyl ester as raw materials. Each component is interacted and interacted with each other and improves the strength and toughness of the prepared composite material. It is suitable for the shell of a robot. Use.
【技术实现步骤摘要】
一种机器人壳体用复合材料及其制备方法
本专利技术涉及复合材料
，尤其涉及一种机器人壳体用复合材料及其制备方法。
技术介绍
机器人作为一种包含相当多学科知识的技术,几乎是伴随着人工智能锁产生的。而智能机器人在当今社会变得越来越重要，大量的领域和岗位都需要机器人的参与，从而使得机器人的研究逐渐得到重视，并且，机器人壳体用材料也是决定机器人性能的重要因素。现有技术中，复合材料及其制备方法得到了广泛的报道，例如，申请号为201180045187.1的中国专利文献报道了一种含有木质纤维材料和聚合物的挤出复合材料。所述木质纤维材料是木节或树枝含量为至少10重量％的木质材料；或者树皮；或者其中已经吸收了通过提取木节、树枝或树皮获得的提取物质的木质材料。所述聚合物的量为所述复合材料的重量的5-25％。申请号为201280061149.X的中国专利文献报道了一种复合材料，在具备树脂或橡胶、以及氧化物玻璃的复合材料中，所述树脂或橡胶分散于所述氧化物玻璃中，或所述氧化物玻璃分散于所述树脂或橡胶中，通过加热，所述氧化物玻璃在所述树脂或橡胶的热分解温度以下软化流动。申请号为20148...
【技术保护点】
1.一种机器人壳体用复合材料，其特征在于，采用如下原料制备：环氧树脂30‑50重量份、水杨酸苯酯4‑8重量份、碳化硅微粉1‑5重量份、苯乙烯5‑10重量份、三氧化二锑2‑6重量份、过氧化二叔丁基1‑4重量份、邻苯二甲基二辛酯6‑10重量份。
【技术特征摘要】
1.一种机器人壳体用复合材料，其特征在于，采用如下原料制备：环氧树脂30-50重量份、水杨酸苯酯4-8重量份、碳化硅微粉1-5重量份、苯乙烯5-10重量份、三氧化二锑2-6重量份、过氧化二叔丁基1-4重量份、邻苯二甲基二辛酯6-10重量份。2.根据权利要求1所述的机器人壳体用复合材料，其特征在于，环氧树脂40-50重量份。3.根据权利要求1所述的机器人壳体用复合材料，其特征在于，水杨酸苯酯4-6重量份。4.根据权利要求1所述的机器人壳体用复合材料，其特征在于，碳化硅微粉2-5重量份。5.根据权利要求1所述的机器人壳体用复合材料，其特征在于，苯乙烯5-7重量份。6.根据权利要求1所述的机器人壳体用复合材料，其特征在于，三氧...
【专利技术属性】
技术研发人员：常雪，苏海迪，
申请(专利权)人：柳州璞智科技有限公司，
类型：发明
国别省市：广西,45