The invention relates to a heat treatment process for a blade root milling cutter, which relates to a heat treatment process. The process of heat treatment is: loading card - medium temperature preheating - high temperature heating - 2 classifying, 3, 5 grades - low temperature salt - heat cleaning - straightening - basket backfire (three times) - Cleaning - straightening - antirust treatment - inspection. The beneficial effect of the invention can make the heat treatment process of the blade root milling cutter meet the process requirements, improve the precision of the tool and the use rate of the fixture, reduce the cost of the fixture and the difficulty of the heat treatment, and be suitable for the production of the small size ultra thin cutters.
【技术实现步骤摘要】
一种叶根铣刀的热处理工艺
本专利技术涉及一种热处理工艺,尤其涉及一种叶根铣刀的热处理工艺。
技术介绍
超薄件一般是指厚度比小于1/20的工件。超薄刀具在刀具热处理行业中是一种很难加工的产品。随着各行业生产的发展,企业间的竞争加强,不仅刀具产量加大,刀具内在质量的提高、成本的降低以及刀具复杂程度都上升到一个新高度。超薄刀具也是这样,叶根铣刀就是一个极具代表性的个例。它不仅是一种超薄件,而且其有效尺寸变化极多,刀具精度也很高,这都增加了产品的热处理难度。由于其形状复杂,如按以往经验生产,除所需卡具制作难度大外,其产品批次少,造成卡具使用率低,也使卡具成本提高。同时,由于该产品加工难度大。
技术实现思路
本专利技术的目的是提供一种叶根铣刀的热处理工艺,降低了其热处理难度。本专利技术是通过以下方式实现的:该热处理工艺路线为:装卡—中温预热—高温加热—2-3-5分级—低温硝盐—热清洗—校直—装筐回火(三次)—清洗—校直—防锈处理—检查。该热处理工艺包括以下几个步骤:(1)中温预热:850-900℃,6分钟;(2)高温加热:1220℃,3分钟;(3)2-3-5分级:550-650℃;(4)低温硝盐:280-290℃;(5)冷却:580-620℃,3分钟;270-280℃,120分钟;(6)回火:560℃,60分钟,三次。经过热处理后的叶根铣刀硬度为64-66HRC,平面度≤0.4mm。本专利技术的有益效果为:采用上述工艺,可以使叶根铣刀的热处理工序达到工艺要求,提高了刀具的精度和卡具的使用率,降低卡具的成本和热处理难度,适合小批量超薄刀具的生产。具体实施方式该热处理工艺包 ...
【技术保护点】
一种叶根铣刀的热处理工艺,其特征在于:该热处理工艺路线为:装卡—中温预热—高温加热—2‑3‑5分级—低温硝盐—热清洗—校直—装筐回火(三次)—清洗—校直—防锈处理—检查。
【技术特征摘要】
1.一种叶根铣刀的热处理工艺,其特征在于:该热处理工艺路线为:装卡—中温预热—高温加热—2-3-5分级—低温硝盐—热清洗—校直—装筐回火(三次)—清洗—校直—防锈处理—检查。2.根据权利要求1所述的叶根铣刀的热处理工艺,其特征在于:该热处理工艺包括以下几个步骤:(1)中温预热:850-900℃,6分钟;(2)高温加热:1...
【专利技术属性】
技术研发人员:曲立辉,
申请(专利权)人:青岛小米星电子科技有限公司,
类型:发明
国别省市:山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。