A wood putty powder without polyvinyl alcohol belongs to the field of building filling materials. The wood putty powder is made from the following raw material: 5 vinyl acetate 10, 3 butyl acrylate, 7, 0.1 hydrochloric acid, 1 sodium hydroxide, 0.1 sodium hydroxide 1, calcium carbonate 20 30 copies, 0.04 sodium base bentonite 0.08, hydroxypropyl methyl cellulose HPMC0.15 0.2 copies, acrylamide 0.05 0.05 5 copies. The invention has the advantages of smooth and delicate, strong sealing, strong adhesion, good solubility, no falling off, simple operation and stable quality. Without using polyvinyl alcohol, the process is simple and safe. The components of the invention are safe and environment-friendly, and do not produce volatile harmful gases.
【技术实现步骤摘要】
一种不含聚乙烯醇的木器腻子粉
本专利技术涉及一种不含聚乙烯醇的木器腻子粉，属于建筑填充材料领域。
技术介绍
木器漆作为木器家具装饰的主要涂装材料，不仅可以美化居室环境，还能够对木器家具起到很好的保护作用，并延长木器家具的使用寿命。目前，许多木器生产厂所用的木器腻子主要有猪血灰和原子灰，但是都存在着不少的问题，例如猪血灰存在不环保、有异味、保质期短、附着力差、封闭性差、易脱落等缺点，原子灰存在干后难打磨、需现调现用及不能调颜色等缺点。传统用建材聚乙烯醇作为腻子胶粉，需加热熬制，必须加入甲醛才可以缩合，反应对人体有害，残留的甲醛也是室内污染的罪魁祸首；而且其成膜性、保水性、增稠性等性能都不是很理想。
技术实现思路
本专利技术的目的是提供一种不含聚乙烯醇的木器腻子粉。本专利技术的技术方案包括如下：本专利技术木器腻子粉由以下重量份的原料制成：醋酸乙烯5-10份、丙烯酸丁酯3-7份、盐酸0.1-1份、氢氧化钠0.1-1份、轻质碳酸钙20-30份、钠基膨润土0.04-0.08份、羟丙基甲基纤维素HPMC0.15-0.2份、丙烯酰胺0.05-0.1份、海菜粉2-5份。本专利技术的有益效果是：本专利技术光滑细腻，封闭性强，附着力强，相溶性好，不脱落，且操作简单，质量稳定。不使用聚乙烯醇，制作工艺简单且安全环保。本专利技术成分安全环保，不会产生挥发性有害气体。具体实施方式以下结合技术方案详细叙述本专利技术的具体实施方式。实施例1醋酸乙烯10份、丙烯酸丁酯7份、盐酸1份、氢氧化钠1份、轻质碳酸钙30份、钠基膨润土0.08份、羟丙基甲基纤维素HPMC0.2份、丙烯酰胺0.1份、海菜...
【技术保护点】
一种不含聚乙烯醇的木器腻子粉，其特征在于，所述的木器腻子粉由以下重量份的原料制成：醋酸乙烯5‑10份、丙烯酸丁酯3‑7份、盐酸0.1‑1份、氢氧化钠0.1‑1份、轻质碳酸钙20‑30份、钠基膨润土0.04‑0.08份、羟丙基甲基纤维素HPMC0.15‑0.2份、丙烯酰胺0.05‑0.1份、海菜粉2‑5份。
【技术特征摘要】
1.一种不含聚乙烯醇的木器腻子粉，其特征在于，所述的木器腻子粉由以下重量份的原料制成：醋酸乙烯5-10份、丙烯酸丁酯3-7份、盐酸0.1-1份、氢氧化钠0...
【专利技术属性】
技术研发人员：刘更新，
申请(专利权)人：青岛赛泽网络科技有限公司，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。