The invention relates to an active carbon putty powder without polyvinyl alcohol, which belongs to the field of building filling materials. The invention is made of the following raw materials: activated carbon, kaolin, attapulgite clay, calcium oxide, anhydrous calcium sulfate, heavy calcium carbonate, montmorillonite inorganic gel, sodium bentonite, acrylamide, corn starch, diatomite, mica powder, carboxymethyl cellulose sodium, zeolite. The invention has the property of water resistance and caking, and the structure of the putty layer after scraping is compact, anti cracking, non skin lifting and non falling off, and the operation is simple and the quality is stable. Without using polyvinyl alcohol, the process is simple and safe. The invention has certain absorbability to formaldehyde and other harmful gas gases.
【技术实现步骤摘要】
一种不含聚乙烯醇的活性炭腻子粉
本专利技术涉及一种不含聚乙烯醇的活性炭腻子粉,属于建筑填充材料领域。
技术介绍
腻子是漆类施工前,对施工面进行预处理的一种表面填充材料,目的在于填充施工面的孔隙及矫正施工面的曲线偏差,为获得均匀、平滑的漆面打好基础,故应具备良好的粘结强度以及耐水性,以保证在空气中水蒸汽的长期侵蚀下不会出现空鼓、起皮、开裂等现象而仍然能够与基体紧密结合,起到良好的装饰与保护作用。传统用建材聚乙烯醇作为腻子胶粉,需加热熬制,必须加入甲醛才可以缩合,反应对人体有害,残留的甲醛也是室内污染的罪魁祸首;而且其成膜性、保水性、增稠性等性能都不是很理想。现有腻子粉的主要指标是抗龟裂、不起皮、不脱落,具有一定的硬度和耐水性。随着社会进步,人们对腻子粉的功能要求也逐渐提高,除了一般的要求外,还需考虑可吸附有害杂质的诉求。如何开发出一种即环保、节能、施工便利,又能具有吸附性的腻子粉已成为今后腻子发展的趋势。
技术实现思路
本专利技术的目的是提供一种不含聚乙烯醇的活性炭腻子粉。本专利技术的技术方案包括如下:本专利技术活性炭腻子粉由以下重量份的原料制成:活性炭5-10份、高岭土8-10份、凹凸棒粘土9-12份、氧化钙2-5份、无水硫酸钙2-4份、重质碳酸钙2-4份、蒙脱石无机凝胶0.2-0.3份、钠基膨润土0.04-0.08份、丙烯酰胺0.05-0.1份、玉米淀粉0.01-0.02份、硅藻土7-13份、云母粉1-3份、羧甲基纤维素钠0.5-1份、沸石1-2份。本专利技术的有益效果是:本专利技术具有耐水性与粘结性,刮涂后腻子层结构致密,抗龟裂、不起皮、不脱落,且操作简单 ...
【技术保护点】
一种不含聚乙烯醇的活性炭腻子粉,其特征在于,所述的活性炭腻子粉由以下重量份的原料制成:活性炭5‑10份、高岭土8‑10份、凹凸棒粘土9‑12份、氧化钙2‑5份、无水硫酸钙2‑4份、重质碳酸钙2‑4份、蒙脱石无机凝胶0.2‑0.3份、钠基膨润土0.04‑0.08份、丙烯酰胺0.05‑0.1份、玉米淀粉0.01‑0.02份、硅藻土7‑13份、云母粉1‑3份、羧甲基纤维素钠0.5‑1份、沸石1‑2份。
【技术特征摘要】
1.一种不含聚乙烯醇的活性炭腻子粉,其特征在于,所述的活性炭腻子粉由以下重量份的原料制成:活性炭5-10份、高岭土8-10份、凹凸棒粘土9-12份、氧化钙2-5份、无水硫酸钙2-4份、重质碳酸钙2-4...
【专利技术属性】
技术研发人员:刘更新,
申请(专利权)人:青岛赛泽网络科技有限公司,
类型:发明
国别省市:山东,37