The invention relates to a radiation proof putty powder without polyvinyl alcohol, belonging to the field of building filling materials. The radiation proof putty is made from the following raw material: 20 white cement, 50 barium sulfate, 65, 10, 15, 0.2, 0.3, 0.08 sodium bentonite, 0.05 acrylamide, 0.1, corn starch 0.01 0.02. The invention has the advantages of water resistance and cohesiveness, compact structure of putty layer after scraping, simple operation and stable quality. Without using polyvinyl alcohol, the process is simple and safe. The invention has strong shielding, high hardness, crack proof and washable, and is suitable for the decoration materials on the building property, especially the first choice of the radiation working environment such as hospitals and scientific research institutions.
【技术实现步骤摘要】
一种不含聚乙烯醇的防辐射腻子粉
本专利技术涉及一种不含聚乙烯醇的防辐射腻子粉，属于建筑填充材料领域。
技术介绍
腻子是漆类施工前，对施工面进行预处理的一种表面填充材料，目的在于填充施工面的孔隙及矫正施工面的曲线偏差，为获得均匀、平滑的漆面打好基础，故应具备良好的粘结强度以及耐水性，以保证在空气中水蒸汽的长期侵蚀下不会出现空鼓、起皮、开裂等现象而仍然能够与基体紧密结合，起到良好的装饰与保护作用。传统用建材聚乙烯醇作为腻子胶粉，需加热熬制，必须加入甲醛才可以缩合，反应对人体有害，残留的甲醛也是室内污染的罪魁祸首；而且其成膜性、保水性、增稠性等性能都不是很理想。现有腻子粉的主要指标是抗龟裂、不起皮、不脱落，具有一定的硬度和耐水性。随着社会进步，人们对腻子粉的功能要求也逐渐提高，除了一般的要求外，还需考虑防辐射的诉求。如何开发出一种即环保、节能、施工便利，又能防辐射的腻子粉已成为今后腻子发展的趋势。
技术实现思路
本专利技术的目的是提供一种不含聚乙烯醇的防辐射腻子粉。本专利技术的技术方案包括如下：本专利技术防辐射腻子粉由以下重量份的原料制成：白水泥20-35份、硫酸钡50-65份、灰钙粉10-15份、蒙脱石无机凝胶0.2-0.3份、钠基膨润土0.04-0.08份、丙烯酰胺0.05-0.1份、玉米淀粉0.01-0.02份。本专利技术的有益效果是：本专利技术具有耐水性与粘结性，刮涂后腻子层结构致密，且操作简单，质量稳定。不使用聚乙烯醇，制作工艺简单且安全环保。本专利技术屏蔽性强，高硬，防裂，耐水洗，适用于广大建筑物业上装饰材料，尤其是是医院，科研机构等辐射工作环境的首选。...
【技术保护点】
一种不含聚乙烯醇的防辐射腻子粉，其特征在于，所述的防辐射腻子粉由以下重量份的原料制成：白水泥20‑35份、硫酸钡50‑65份、灰钙粉10‑15份、蒙脱石无机凝胶0.2‑0.3份、钠基膨润土0.04‑0.08份、丙烯酰胺0.05‑0.1份、玉米淀粉0.01‑0.02份。
【技术特征摘要】
1.一种不含聚乙烯醇的防辐射腻子粉，其特征在于，所述的防辐射腻子粉由以下重量份的原料制成：白水泥20-35份、硫酸钡50-65份、灰钙粉...