The invention relates to a multifunctional environment-friendly desulfurized gypsum block and its processing technology, which belongs to the technical field of building materials. The gypsum block is made of desulphurized gypsum powder and fly ash. The raw material and water are made in proportion to 0.75: 1. The weight percentage of the desulphurized gypsum is 89%, and the weight percentage of the fly ash is 11%. The invention is a comprehensive utilization of industrial waste resources, product raw material is industrial waste, low cost, high quality product. It is a kind of high grade inner wall material, which integrates safety, comfort, environmental protection and health. It has light quality, environmental protection, moisture proof, water resistance, heat insulation, sound absorption, insulation, good fire prevention, sound insulation and so on. Point.
【技术实现步骤摘要】
一种多功能绿色环保脱硫石膏砌块及加工工艺
本专利技术涉及一种多功能绿色环保脱硫石膏砌块及加工工艺,属于建筑材料
技术介绍
在建筑工程上,石膏砌块常用于房间的内隔墙。现有的石膏砌块存有以下缺陷:强度和韧性低,空心砌块在上钉之前需埋入预埋件;隔热、隔音、防潮效果较差;无保温效果;抗阻声音和防火性能也较差;重量大、占地面积大;结构单一。
技术实现思路
本专利技术的目的之一在于,提供一种多功能绿色环保脱硫石膏砌块,以解决现有技术中存在的技术问题。本专利技术是通过以下技术方案来实现的:一种多功能绿色环保脱硫石膏砌块,其特征在于:采用由脱硫石膏粉和粉煤灰配制而成的原料与水按照0.75∶1的比例制成;所述的原料中,脱硫石膏的重量百分比为89%,粉煤灰的重量百分比为11%。本专利技术的另一目的在于,提供一种多功能绿色环保脱硫石膏砌块的加工工艺,其特征在于:包括如下步骤:1.按照脱硫石膏粉89%、粉煤灰11%配制好原料,再以配制好的原料重量为基准,按照原料∶水=0.75∶1的比例称量水;2.先将水倒入搅拌机内,加入粉煤灰,搅拌30秒后,再加入脱硫石膏粉搅拌60秒;3.倒入砌块成型机,刮平,120秒后成型起模;4.利用工业废蒸汽进行弱氧强化干燥烘干,即得成品。本专利技术是对工业废弃物(工业废渣、废水、废蒸汽)的资源综合利用,产品原料为工业废弃物,成本低,产品品质高,是一种集安全、舒适、环保、健康为一体的高档内隔墙材料,具有轻质、环保、防潮、耐水、隔热、吸音、保温和很好的防火、隔音等特点。具体地说,本专利技术具有以下优点:1、本专利技术烧注成型后,不龟裂、不变形,而且具有 ...
【技术保护点】
一种多功能绿色环保脱硫石膏砌块,其特征在于:采用由脱硫石膏粉和粉煤灰配制而成的原料与水按照0.75∶1的比例制成;所述的原料中,脱硫石膏粉的重量百分比为89%,粉煤灰的重量百分比为11%。
【技术特征摘要】
1.一种多功能绿色环保脱硫石膏砌块,其特征在于:采用由脱硫石膏粉和粉煤灰配制而成的原料与水按照0.75∶1的比例制成;所述的原料中,脱硫石膏粉的重量百分比为89%,粉煤灰的重量百分比为11%。2.如权利要求1所述多功能绿色环保脱硫石膏砌块的加工工艺,其特征在于:包括如下步骤:(1)按照脱...
【专利技术属性】
技术研发人员:宁一霖,
申请(专利权)人:宁波讴芬诺化工有限公司,
类型:发明
国别省市:浙江,33