一种聚酯薄膜制造技术
A kind of polyester film
The invention discloses a polyester film, including a substrate and a bottom coating coated on a surface of a substrate, a back coating on the other surface of the base material, and a random particle in the back coating. The back coating is formed by UV curing by the following coating composition: 15 weight portions of acrylic resin to 50 weight, Polyester resin 3 weight to 15 weight parts, photoinitiator 0.2 weight to 5 parts, leveling agent 0.01 weight to 0.5 weight, particle 0.5 to 5 parts, 0.05 antistatic weight to 2 weight, organic solvent 20 weight to 70 parts. The invention uses the coating composition containing polyester resin to make the back coating, improves the adhesion of the back coating on the polyester film, reduces the use of the bottom coating, improves the rate of finished products, reduces the cost, and can be widely applied to the brightening film of various structures.
【技术实现步骤摘要】
一种聚酯薄膜
本专利技术属于光学薄膜领域，特别涉及液晶显示器的背光模组用的聚酯薄膜。
技术介绍
用于液晶显示器的背光模组由多种光学膜叠加而成，一般的架构中，自下而上(往液晶屏方向)依次包括反射膜、扩散膜、增亮膜、增亮膜、扩散膜，这些膜片组合起来的作用是最大效率地利用背光模组中的光能，将光线利用并以最大效率集中投射向使用者方向。常见的增亮膜是由一平板状基板和多个可以汇聚光线的棱镜组成。增亮膜在生产过程中为了能正常收卷，一般会在增亮膜所用的基膜上设背涂层。背涂层中含有微粒子，用于减小增亮膜收卷时的摩擦力、提高收卷时的成品率；同时，背涂层还应有一定的雾度，用于掩盖整个背光模组的瑕疵、弊病。增亮膜用的背涂层，目前的技术基本上都是紫外固化涂料在聚酯薄膜上固化而成，由于聚酯薄膜表面是惰性的，一般的涂料很难在在聚酯薄膜上附着，所以，现有技术都是在聚酯薄膜上先涂覆一层底涂层，通过底涂层可以提高背涂层在聚酯薄膜上的附着力。底涂层可以解决附着力的问题，但是底涂层的使用，增加了聚酯薄膜的制造成本，降低了良品率。
技术实现思路
本专利技术要解决的技术问题是针对现有技术存在的上述问题，提供一种...
【技术保护点】
一种聚酯薄膜，包括基材(1)和涂覆在基材一个表面上的底涂层(2)，其特征在于，在基材另一个表面直接设有背涂层(3)，背涂层中随机分布有微粒子(4)，所述背涂层是由以下涂层组合物经过紫外光固化形成：
【技术特征摘要】
1.一种聚酯薄膜，包括基材(1)和涂覆在基材一个表面上的底涂层(2)，其特征在于，在基材另一个表面直接设有背涂层(3)，背涂层中随机分布有微粒子(4)，所述背涂层是由以下涂层组合物经过紫外光固化形成：2.根据权利要求1所述的聚酯薄膜，其特征在于，所述丙烯酸树脂是官能度4～15的(甲基)丙烯酸酯预聚物、(甲基)丙烯酸酯单体或它们的组合物。3.根据权利要求1所述的聚酯薄膜，其特征在于，所述聚酯树脂是丙烯酸改性的不饱和聚酯树脂。4.根据权利要求1所述的聚酯...
【专利技术属性】
技术研发人员：刘玉磊，王辉，李恒，王巧，万金龙，何晶晶，朱用国，
申请(专利权)人：合肥乐凯科技产业有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。